专利汇可以提供Method of fabricating heteroepitaxial microstructures专利检索,专利查询,专利分析的服务。并且An efficient method of fabricating a high-quality heteroepitaxial microstructure having a smooth surface. The method includes detaching a layer from a base structure to provide a carrier substrate having a detached surface, and then forming a heteroepitaxial microstructure on the detached surface of the carrier substrate by depositing an epitaxial layer on the detached surface of a carrier substrate. Also included is a heteroepitaxial microstructure fabricated from such method.,下面是Method of fabricating heteroepitaxial microstructures专利的具体信息内容。
What is claimed is:
This application is a continuation of application Ser. No. 10/700,899 filed Nov. 3, 2003 U.S. Pat. No. 6,946,317, and a continuation-in-part of copending application 10/922,997 filed Aug. 23, 2004 which is a continuation of application 10/446,605 filed May 27, 2003, now U.S. Pat. No. 6,794,276, which in turn is a continuation of International application PCT/FR01/03714 filed Nov. 26, 2001, the entire content of each of which is expressly incorporated herein by reference thereto.
The present invention relates to an efficient and cost effective method of fabricating a microstructure. The method includes detaching a carrier structure to provide a base substrate having a detached surface, and depositing an epitaxial layer on the detached surface of the base substrate. The present invention also relates to the microstructure formed from such method.
Generally, it is known that crystalline microstructures may be fabricated by forming an epitaxial gallium nitride layer on an α-Al2O3 substrate. Typically, such microstructures include a buffer layer such as aluminum nitride between the gallium nitride and the α-Al2O3 so that the lattice constant mismatch between the gallium nitride layer and the α-Al2O3 substrate materials is reduced.
It is also known that crystalline microstructures may be fabricated without buffer layers when the gallium nitride layer epitaxial layer is formed on a base substrate of silicon carbide, silicon or another material that is compatible with the gallium nitride epitaxy.
Additionally, the formation of SiGe layers by epitaxial growth on flat surfaces is also known.
In order to produce crystalline microstructures that have a deposited epitaxial layer with good crystal quality, the base substrate or carrier must have a smoothly finished surface. Thus, it has been necessary to polish such surfaces to obtain a base substrate having very low surface roughness. The polishing steps necessary to achieve smoothly finished base substrates are time-consuming, costly, and have low efficiency. Moreover, such polishing steps are particularly difficult when materials such as SiC are to be polished. Silicon carbide and other similar materials can only be polished with a very low efficiency due to their thinness and hardness qualities. Thus, such materials are typically provided having an increased surface roughness and defects such as surface scratches. These drawbacks have lead those skilled in the art to the opinion that SiC substrates are not suitable for fabricating high quality heteroepitaxial structures, such as structures with a gallium nitride layer.
Thus, there is a need for a more efficient method for fabricating a microstructure, especially a heteroepitaxial microstructure, with high crystal quality and a high degree of surface smoothness, and to provide a high quality microstructure with a smooth surface which can be fabricated efficiently.
The present invention satisfies that need by providing an efficient method for fabricating a microstructure comprising the steps of detaching a layer from a base structure to provide a carrier substrate having a detached surface, and forming a microstructure on the detached surface of the carrier substrate by depositing a first epitaxial layer thereon. It has surprisingly been found that a base substrate formed in this way has very smooth detached surface and is especially well-suited for forming an epitaxial layer with a high crystal quality and an excellent level of smoothness.
Advantageously, the microstructure formed from a base substrate having a detached surface and a deposited epitaxial layer is fabricated with less time and effort typically required for fabricating the microstructure of the prior art. Additionally, if desired, the detached surface may be treated or further polished.
In one embodiment of the invention, the detaching process for detaching the carrier surface to provide the base substrate is includes the implantation of species into the carrier structure, and subjecting the implanted structure to thermal annealing. The species include for illustration and not limitation, hydrogen ions, and rare gases. Advantageously, the characteristics of the detached carrier surface can be controlled by adjusting the parameters of the detaching process, such as the implantation dose used, the species chosen, the backing method used or the annealing parameters, which can lead to a defined morphology of those surfaces. The final detaching can be accompanied by a mechanical step.
Preferably, the detached surface has a surface roughness with RMS values of about 5 Å to 150 Å, especially 20 Å to 100 Å or 20 Å to 60 Å. This roughness allows a very good nucleation, providing a high-quality growth of the epitaxial layer on this surface.
The epitaxial layer comprises at least one of the following materials aluminum nitride, gallium aluminum nitride, silicon germanium, germanium, InGaN or gallium nitride. It has been shown that these layers grow especially well on the detached carrier surface.
The carrier structure comprises at least one of the following materials sapphire, silicon carbide, silicon, germanium, gallium arsenide, lithium gallate, indium phosphide, lithium aluminate, ZnO, aluminum nitride or gallium nitride. These materials can be easily detached and are appropriate for an epitaxial formation of a crystalline layer thereon. It is particularly favourable when the carrier structure is a composite structure, comprising at least a base wafer and a single crystalline top layer having the detached surface. In this microstructure, the crystalline top layer can accommodate very well strain caused by a lattice constant mismatch between the base wafer and the epitaxial layer.
In another embodiment of the invention, a first epitaxial layer is used as a buffer layer on which a second epitaxial layer is formed. Advantageously, the buffer layer, a lattice constant mismatch between the carrier substrate and the second epitaxial layer can be reduced, resulting in a high quality formation of the second epitaxial layer. Preferably, the second epitaxial layer comprises gallium nitride or relaxed silicon germanium. In one aspect of the invention the GeSi can be combined with other layers made from materials such as but not limited to strained silicon or germanium together forming the second epitaxial layer.
This method of the present invention produces a high-quality microstructure which is very attractive for many electronic and opto-electronic devices. The wide, direct energy band gap of the nearly-perfect gallium nitride which can be formed by the inventive method makes it suitable, for instance, for short wave length emitters and detectors. And its good thermal stability is advantageous for high temperature and high power electronics. Gallium nitride can be combined in an alloy with InGaN, and/or AlGaN, or be combined with layers of the materials together forming the second epitaxial layer.
Also in accordance with the present invention is a microstructure, preferably a heteroepitaxial microstructure, wherein the base substrate is produced by the detaching process described above. Surprisingly, the detached surface of the carrier substrate is very well-suited for depositing the epitaxial layer thereon with a high quality. The epitaxial layer can be formed on the detached carrier surface very easily and with a resulting low thickness, so that the microstructure can be produced with high efficiency.
Preferably, the carrier structure comprises sapphire, silicon carbide, silicon, gallium arsenide, lithium gallate, lithium aluminate, ZnO, aluminum nitride, germanium, indium phosphide, or gallium nitride. These materials can provide good detaching characteristics, leading to detached carrier surfaces on which the epitaxial layer can be formed with high quality. Some of the specified materials further have the advantage that they are compatible materials for a gallium nitride epitaxy, so that they can be effective for formation of epitaxial gallium nitride with a good crystallinity.
Preferably, the epitaxial layer comprises aluminum nitride, gallium aluminum nitride, InGaN or gallium nitride. These materials show very good growth characteristics on the detached carrier surface. More preferably, the epitaxial layer is gallium nitride. This material has very good electronic properties, so that the resulting microstructure can be used with ease in many electronic and opto-electronic devices.
In a further advantageous embodiment of the invention, the epitaxial layer is a buffer layer on which a second epitaxial layer is formed. Such a buffer layer is especially favourable for compensating for a lattice constant mismatch between the carrier structure and the second epitaxial layer.
The present invention will be more apparent from the following detailed description with reference to the accompanying figures.
The present invention is directed to a method of fabricating a microstructure comprising the steps of detaching a base structure to provide a carrier substrate having a detached surface; and depositing at least one epitaxial layer on the carrier substrate.
The base structure of the present invention is detached to form a carrier substrate. The detaching step includes implantation of species 4 such as hydrogen ions and/or rare gases, which are implanted through the oxide layer 8, and into wafer 7 to form an implanted carrier structure. The dose and/or energy of the implanted species may be adjusted so that a peak of concentration of the implanted species 4 is formed at a certain depth d on the wafer 7, thereby forming a weakened layer due to the ion implantation 11 at or near this depth d.
The detaching step may includes as shown in
The detached carrier structure 1 as shown in
In a further embodiment of the present invention, the roughness of the detached surface 3 can be further reduced by an additional step after detaching and before growth of a crystalline layer on the surface 3. This additional step can be oxidation and de-oxidation, chemical-mechanical polishing, etching by gas cluster, ion beam or reactive ion etching, HCL-smoothing or a combination of at least two of these steps. For example, the surface 3 can be treated with a thermal oxidation wherein the oxide is removed thereafter and the surface is finished with a final chemical-mechanical polishing step to a certain degree. In this way, the roughness of the surface 3 can be adjusted over a wide range of roughness values. Additionally, the power spectral distribution of the roughness can be shaped by the detaching parameters and/or subsequent treatment steps.
The roughness of the detaching surface 3 is relatively homogeneous, even after the detaching process. When the detached surface 3 is treated with at least one of the above-mentioned additional steps, the surface roughness can be tuned from a high roughness value of the just-detached surface to a low roughness value, wherein the homogeneity of the overall roughness of the surface 3 is maintained. After a thermal treatment, an ion treatment or a chemical-mechanical polishing, the carrier surface 3 has a roughness with RMS values of about 5 Å up to the roughness values of the detached surface 3 directly after detaching.
As shown in
A microstructure fabricated from the method of the invention is illustrated in
Further, a chemical-mechanical polishing step can be added, if necessary, between the growth of epitaxial layer 2 and epitaxial layer 5.
Also in accordance with the invention is a microstructure comprising first and second epitaxial layers. As illustrated in
With reference to
Specifically, the resulting microstructure 13 preferably consists of an α-Al2O3 or SiC base wafer 6, silicon dioxide insulator layers 8, 8′ thereon, and a residual part 7′ of a further α-Al2O3 wafer 7. On the detached surface 3 of the layer 7′, a thin aluminum nitride layer 2 is formed, and the layer thereon is a monocrystalline gallium nitride layer 5.
标题 | 发布/更新时间 | 阅读量 |
---|---|---|
基于表面等离激元的硅基纳米激光器及其制备方法 | 2020-05-08 | 385 |
一种发光二极管外延片及其制备方法 | 2020-05-11 | 238 |
一种基于转印技术的平面隧穿场效应晶体管及其制备方法 | 2020-05-13 | 24 |
一种基于互补型SiC的新型晶体管器件及其制备方法 | 2020-05-08 | 675 |
一种高质量氧化镓薄膜及其同质外延生长方法 | 2020-05-12 | 820 |
集成背面垂直型和正面水平型三维磁场探测功能的高温霍尔传感器及其制作方法 | 2020-05-12 | 125 |
包含单个晶格匹配的稀释氮化物结的薄膜柔性光电器件及制造方法 | 2020-05-13 | 72 |
具有2D材料中介层的外延基板及制备方法和制作组件 | 2020-05-08 | 565 |
一种半导体器件纳米线及其制备方法 | 2020-05-12 | 969 |
一种增强型AlN/AlGaN/GaN HEMT器件 | 2020-05-08 | 242 |
高效检索全球专利专利汇是专利免费检索,专利查询,专利分析-国家发明专利查询检索分析平台,是提供专利分析,专利查询,专利检索等数据服务功能的知识产权数据服务商。
我们的产品包含105个国家的1.26亿组数据,免费查、免费专利分析。
专利汇分析报告产品可以对行业情报数据进行梳理分析,涉及维度包括行业专利基本状况分析、地域分析、技术分析、发明人分析、申请人分析、专利权人分析、失效分析、核心专利分析、法律分析、研发重点分析、企业专利处境分析、技术处境分析、专利寿命分析、企业定位分析、引证分析等超过60个分析角度,系统通过AI智能系统对图表进行解读,只需1分钟,一键生成行业专利分析报告。