专利汇可以提供Manufacture of ultra low carbon, fine grain, high tensile steel with superior hydrogen induced cracking resistance专利检索,专利查询,专利分析的服务。并且PURPOSE: To manufacture a high tensile steel with superior strength, toughness and hydrogen induced cracking resistance by reducing the C content of steel to enhance the hydrogen induced cracking resistance; adding Mn to offset a lowering in strength; and carrying out specific heat treatment to lower the hydrogen induced cracking sensibility.
CONSTITUTION: An ultra low carbon steel contg. C; 0.001W0.01%, Si 3 pointW1150°C to be austenitized, and then it is hot rolled at a reduction ratio above 60% at below 850°C to make the grains fine. Tempering temp. is regulated to 550°Wthe Ac
1 point, thus obtaining a high tensile steel with superior hydrogen induced cracking resistance.
COPYRIGHT: (C)1979,JPO&Japio,下面是Manufacture of ultra low carbon, fine grain, high tensile steel with superior hydrogen induced cracking resistance专利的具体信息内容。
标题 | 发布/更新时间 | 阅读量 |
---|---|---|
一种脖挂式防爆抗噪蓝牙耳机 | 2020-05-08 | 622 |
用于流量治疗设备的流动路径感测 | 2020-05-12 | 468 |
一种振动筛装置 | 2020-05-14 | 228 |
一种难降解废水处理工艺 | 2020-05-08 | 617 |
包括应力抵消树脂层的低光泽黑色聚酰亚胺薄膜及其制备方法 | 2020-05-11 | 843 |
装配式钢结构梁柱连接节点及施工方法 | 2020-05-17 | 751 |
一种挂车车架加工工艺 | 2020-05-08 | 666 |
一种提高铜精矿中银含量测定准确性的方法 | 2020-05-08 | 931 |
一种抗震结构的易拉罐 | 2020-05-15 | 790 |
排氣管消音結構 | 2020-05-15 | 49 |
高效检索全球专利专利汇是专利免费检索,专利查询,专利分析-国家发明专利查询检索分析平台,是提供专利分析,专利查询,专利检索等数据服务功能的知识产权数据服务商。
我们的产品包含105个国家的1.26亿组数据,免费查、免费专利分析。
专利汇分析报告产品可以对行业情报数据进行梳理分析,涉及维度包括行业专利基本状况分析、地域分析、技术分析、发明人分析、申请人分析、专利权人分析、失效分析、核心专利分析、法律分析、研发重点分析、企业专利处境分析、技术处境分析、专利寿命分析、企业定位分析、引证分析等超过60个分析角度,系统通过AI智能系统对图表进行解读,只需1分钟,一键生成行业专利分析报告。