Dielectric compositions stabilized against water treeing with organo silane compounds and electric wires or cables insulated with these compositions
专利汇可以提供Dielectric compositions stabilized against water treeing with organo silane compounds and electric wires or cables insulated with these compositions专利检索，专利查询，专利分析的服务。并且Dielectric compositions comprising ethylene polymers which are susceptible to electrical breakdown by water treeing are protected against such breakdown by the incorporation therein of organo silanes.，下面是Dielectric compositions stabilized against water treeing with organo silane compounds and electric wires or cables insulated with these compositions专利的具体信息内容。
This invention relates to inhibiting electrical break-down by water treeing in dielectric materials which are based on ethylene polymers.
Compositions based on polyolefins are well known and they are used extensively as insulation materials for wire and cable. As insulation materials, properties of the composition such as intrinsic electrical strength, corona resistance and i resistance to treeing are important.
Intrinsic electrical breakdown is the catastrophic failure of a dielectric accompanied by arcing or discharge through an ionized channel in the dielectric. The intrinsic dielectric strength is considered to be an inherent property of the dielectric material.
In power cable applications for transmitting relatively high voltage loads such as 5KV and above, corona may be a problem because it may lead to the premature breakdown of the cable insulation. Corona is an electrical plasma resulting from the ionization of a gaseous dielectric in regions of high electrical field. Corona resistance is the ability of a ! dielectric to withstand the corrosive action of an electrical field. Corona resistance is the ability of a dielectric to withstand the corrosive action of an electrical plasma in contact with it.
When used as a high voltage power cable insulation, olefin base compositions undergo a prebreakdown phenomenon known as treeing. This type of damage progresses through a dielectric section under electrical stress so that, if visible its path looks something like a tree. Treeing can occur and progress slowly by periodic partial discharge, it may occur slowly in the presence of moisture without any partial discharge, or it may occur rapidly as the result of an impulse voltage. Trees may form at sites of high electrical stress such as contaminants or voids in the body of the insulation or at irregularities at the insulation- semiconductive screen interface.
In solid organic dielectrics treeing is the most likely mechanism of electrical failures which do not occur catastrophically, but rather appear to be the result of a more lengthy process. It is desired to extend the service liefe of olefin-insulated cables by modification of the insulating materials so that trees are initiated at higher voltages than usual or so that the rate of growth of trees is reduced once initiated.
Electrical treeing results from internal electrical discharges which decompose the dielectric. Although high voltage impulses can produce electrical trees, and the presence internal voids and contaminants is undesirable, the damage which results from application of moderate a.c. voltages to electrode/insulation interfaces which contain imperfections is more commercially significant. In this case very high, localized stress gradients can exist and with sufficient time lead to initiation and growth of trees which may be followed by breakdown. An example of this is a high voltage power cable or connector with a rough interface between the conductor or conductor shield and the primary insulator. The failure mechanism involves actual breakdown of the modular structure of the dielectric material perhaps by electron bombardment. Much of the prior art is concerned with the inhibition of electrical trees.
Water treeing is a deterioration of a solid dielectric material which is simultaneously exposed to moisture and an electric field. It is a significant factor in determining the useful life of buried high voltage power cables. Wate" trees initiate from sites of high electrical stress such rough interfaces, protruding conductive points, voids, or imbedded contaminants but at a lower field than that require for electrical trees. In contrast to electrical trees, water trees are characterized by:
- (a) the presence of water is essential for their growth;
- (b) no partial discharge is normally detected during theii growth;
- (c) they can grow for years before reaching a size where they may contribute to a breakdown;
- (d) although slow growing, they are initiated and grow in much lower electrical fields than those required for the development of electrical trees.
Thus, intrinsic electrical breakdown, failure by corona, electrical treeing and water treeing are different and the mechanisms for each are different. It follows that a different solution is required to effect improvement in a dielectric material for each mode of failure involved.
Additionally, it is known that when crosslinked olefin polymers, particularly polyethylene, are used for power cable insulation, a crosslinking agent may function as a water treeing inhibitor. When dicumyl peroxide is used as the crosslinking agent in polyethylene, for example, the peroxide residue functions as a tree inhibitor for some time after curing. However, these residues are eventually lost at the temperatures of cable service. Therefore, in order to be an effective water treeing inhibitor an additive must be such that it is retained in the olefin composition at the temperature of cable service.
It has now been found that dielectric compositions based on ethylene polymers and used as insulation materials in high voltage wire and cable are protected from water treeing under long term use under high voltage conditions, if the composition contains as a water treeing inhibitor, one or more organo silanes.
The organo silanes of the present invention have excellent compatibility with ethylene polymers, high retention under cable service temperatures, and resistance to water tree growth.
An object of the present invention is to provide a process for employing dielectric materials as insualtion in high voltage wire and cable while protecting such dielectric material against water treeing.
Another object of the present invention is to provide dielectric materials which are resistant to water treeing in high voltage wire and cable and which retain this resistance under the conditions of use of the wire and cable.
A further object of the present invention is to provide a high voltage wire and cable which is resistant to water treeing.
These and other objects are achieved by employing certain organo silane compounds as water treeing inhibitors in combination with ethylene polymers in the dielectric insulation compositions of the present invention.
The dielectric composition of the present invention comprise, in weight ratio, 100 parts by weight of ethylene polymer, as described below, and about 0.1 to 10, and preferably, about 0.5 to 3.0, parts by weight of at least one of the organo silane compounds which are also described below.
The ethylene polymers which are used in the compositions of the present invention are solid (at 25oC) materials which may be homopolymers, or copolymers of ethylene. The ethylene copolymers contain at least 30 weight percent of ethylene and up to about 70 weight percent of propylene, and/or up to about 50 weight percent of one or more other organic compounds which are interpolymerizable with ethylene. These other compounds which are interpolymerizable with ethylene are preferably those which contain polymerizable unsaturation, such as is present in compounds containing an ethylene linkage,>C = C<. These other interpolymerizable compounds may be hydrocarbon compounds such as, butene-1, pentene-1, isoprene, butadiene, bicycloheptene, bicycloheptadiene, and styrene, as well as vinyl compounds such as vinyl acetate and ethyl acrylate.
These copolymers could thus include those containing > 0 to 70 weight of propylene and 30 to < 100 weight percent of ethylene; and > 0 to < 50 weight percent butene-1 or vinyl acetate and 50 to < 100 weight percent of ethylene; and > 0 to <30 weight percent of propylene, > 0 to 20 weight percent of butene-1 and 50 to < 100 weight of ethylene.
Preferred copolymers are ethylene/ethyl acrylate, ethylene/ propylene, ethylene/butene and the like.
Also included in the term polymer are blends of one polymer with one or more other polymers. Illustrative of such blends are polyethylene with polypropylene, low-density polyethylen with high-density polyethylene, and polyethylene with olefin copolymers such as these indicated above.
The low density ethylene copolymers with α-olefins may be made under low pressure conditions of about 150 to 300 psi with supported chromium oxide based catalysts that are modified with titanium and optionally, fluorine, as disclose in U.S. Patents 3,606,736 and 4,011,382. The disclosure of these patents are included herein by reference.
The ethylene polymers described herein have a density (ASTM 1505 test procedure with conditioning as in ASTM D-1248-72) of about 0.86 to 0.96 grams/cubic centimeter and a Melt Index (ASTM D-1238 at 44 psi test pressure) of about 0.1 to 10 decigrams per minute.
The organo silane which is employed in the dielectric compositions of the present invention is selected from one or more compounds of the following formula:
These organo silanes are prepared by reacting either an aldehyde or a ketone with an aminoalkylsilane as set forth in, for example, U.S. Patent 2,942, 019, which is incorporated herein by reference.
The preferred organo silanes are derived from N-β-(aminoethyl) -γ-aminopropyltrimethoxy silane and γ-aminopropyltriethoxysilane.
In addition to the ethylene polymer and the organo silane, the dielectric compositions of the present invention may also include crosslinking agents where the dielectric composition is to be used as a vulcanized composition rather than as a thermoplastic composition, and it is to be chemically crosslinked. These chemical vulcanizing, curing or crosslinking agents are well known to those in the art and include the organic peroxide type of crosslinking agents which are disclosed for example, in United States Patents 2,826,570, 2,888,424, 2,916,481, 3,079,370 and 3,296,189, the disclosures in such patents being incorporated herein by reference. The chemical crosslinking agents may be used individually or in combination with one another, and they are used in crosslinking effective amounts. The preferred crosslinking agent is di-α-cumyl peroxide.
The dielectric compositions of the present invention also advantageously include one or more suitable high temperature antioxidants for the ethylene polymer in such compositions. The antioxidants include sterically hindered phenols or amines. Polymerized 2,2,4-trimethyl dihydroquinoline may also be used. These are used in conventional amounts to obtain the intended effect in the composition.
Other adjuvants which may be employed in the compositions of the present invention would include adjuvants commonly employed in ethylene polymer based dielectric compositions including lubricants, oil extenders, dyes and colorants, and metal deactivators.
These adjuvants would be used in amounts designed to provide the intended effect in the resulting composition.
The dielectric compositions of the present invention may also be extended, or filled, with polymers other than the ethylene polymer which are compatible, i.e., can be physically blended or alloyed, or grafted with the ethylene polymer. The resulting compositions should contain at least about 30 weight percent of interpolymerized ethylene in all the polymers that may be present in the composition, based on the total weight of the resulting composition. The other polymers which may be used would include polyvinyl chloride and polypropylene, ethylene rubbers (EPR)., ethylene, propylene, diene polymers (EPDM), styrene-butadiene-styrene block copolymers, urethane elastomers, natural rubber.
The total amount of adjuvants used will range from 0 to about 60 weight percent, preferably 0 to 10 weight percent based on the total weight of the dielectric composition.
All of the components of the dielectric compositions of the present invention are usually blended or compounded together prior to their introduction into the extrusion device from which they are to be extruded onto an electrical conductor. The ethylene polymer and the other desired constituents may be blended together by any of the techniques used in the art to blend and compound thermoplastics to homogenous masses. For instance, the components may be fluxed on a variety of apparatus including multi-roll mills, screw mills, continuou mixers, compounding extruders and Banbury mixers. The organo silanes may be prepared in advance or in situ during the compounding step by adding appropriate quantities of aldehyde or ketone and aminosilane. A separate preparation step may be used for less reactive ketones, and a catalyst such as ammonium chloride can be used.
After the various components of the compositions of the present invention are uniformly admixed and blended together they are further processed, in accordance with the process of the present invention, in conventional extrusion apparatus at about 1200 to 160°C for cross-linkable compositions and about 200°C for thermoplastic compositions.
After being extruded onto a wire or cable, or other substrate, the cross-linkable compositions of the present invention are vulcanized at elevated temperatures of about 180°C and preferably at 215-230°C using conventional vulcanizing procedures.
In order to determine the utility and effectiveness of the water treeing stabilized dielectric compositions of the present invention, the compositions were evaluated with the organo silanes incorporated therein by use of an accelerated water tree test which incorporates a combination of frequently acceleration and a standard-defect specimen. The test utilizes a compression molded dish-shaped specimen having 24 conical depressions molded into the bottom. Figure 1 shows a cross sectional view of the specimen, where a is 152.4 millimeters, b is 25.4 millimeters and c is 19.05 millimeters. The conical depression, W, of Figure 1 is magnified in Figure 1A where d is 3.18 millimeters, e is 60 degrees, f is 3.18 millimeters, g is 6.35 millimeters and the tip radius is about 5 pm. The calculated maximum field is about 250 kv/mm in a typical 15 kv power cable.
When testing these specimens, 100 ml. of an electrolyte solution is poured into the dish which is then placed into a grounded bath, usually containing the same electrolyte solution. A 50 millimeter diameter platinum wire ring is then immrsed in the electrolyte in the dish and connected to the voltage source.
Preliminary experiments at 8.5 kHz showed that electrical treeing followed by breakdown rapidly occurred at test voltages of 10kv or above. In order to limit the study to the effects of water treeing, the voltage used in the examples was 5 kv. Under these conditions a low density polyethylene specimen will develop water trees at the tips of the conical depressions between 120 and 240 micrometers in length in 24 hours using 0.01 N NaCl in distilled water as the electrolyte solution.
To facilitate study of the water trees found, each of the twelve conical depressions nearest the center of the specimen is punched out using a 12.7 millimeter (1/2 inch) circular die and an arbor press. The resulting discs are placed in a boiling solution of 0.50 g methylene blue and 8 milliliter concentrated aqueous ammonia (28% approx.) in 250 milliliters distilled water for 30 minutes. The discs are then sectioned and mounted on microscope slides for examination. Specimens prepared in this way have been kept for periods up to two years without apparent deterioration of the appearance of water trees.
A typical water tree grown for 24 hours in low density polyethylene under the above conditions and stained as described, is depicted in Figure 2. The growth occurs in an approximately hemispherical region centered on the tip of the cone, which is usually heavily obscured. Because of this, the most satisfactory direction for measuring the extent of tree growth was found to be perpendicular to the side of the cone as indicated in Figure 2. In our procedure all twelve of the stained trees from the central group of conical depressions are measured and the average length calculated.
The rate of growth of water trees,
If one assumes that water trees are relatively conductive compared to polyethylene, one can calculate the electrical field, E, at the boundry of a growing tree from equation 3 which was derived for the point-to-point geometry of the present test method.
The following examples are merely illustrative of the scope of the present invention and are not intended as a limitation upon the scope thereof.
The dielectric compositions used in the Examples below were all prepared according to the following Procedure A:
Polyethylene homopolymer of 0.2 dg/min Melt Index and 0.92 g/cc density, or ethylene-α-olfin copolymer of 0.8 dg/min Melt Index and density of 0.92 g/cc, organo silane and antioxidant are charged to a Banbury mixer and compounded to a melt temperature of approximately 140°C. The resulting composition was then sheeted on a 2-roll mill, granulated and compression molded into test specimens, as heretofore described, at approximately 165°C.
Water Tree Growth Rate (hereinafter WTGR) is the ratio of rate for the test composition to that of a control. The controls are a commercial grade of high molecular weight polyethylene having a Melt Index of 0.2 dg/minute and a density of 0.918 grams/cubic centimeter and containing 0.10 percent of 4,4'-thiobis (3-methyl-6-tert butyl phenol) antioxidant (Control A); or an ethylene-butene-1 copolymer having a Melt Index of 0.8 dg/minute and a density of 0.92 grams/cubic centimeter and containing 0.10 percent of thiodiethylene-bis (3,5-ditert-butyl-4-hydroxy) hydrocinnamate anitoxidant (Control B). The ingredients of these Controls were mixed according to Procedure A, but without organo silane additive. The water tree growth rate was obtained by measuring the length of water trees formed in 24 hours and calculating the absolute rate of tree growth, as heretofore described by equations (1) to (7). Relative values of 1.0 and 1.03 for water tree growth rate were assigned to Control A and Control B, respectively.
This Example illustrates the formation of the organo silane in situ by adding an aldehyde and amino silane to the polyethylene in the compounding step.
The following were charged to a Banbury mixer:
- 28 pounds of the polyethylene of Control A, 122.4 grams of benzaldehyde and 256 grams of N-B(aminoethyl)-Y-aminopropyltrimethoxysilane.
Mixing was conducted until the melt temperature reached 325°F, after which the charge was dropped to a conventional extruder, stranded and diced. A water tree test specimen was molded at 155oC. as heretofore described. Water tree growth rate was obtained by measuring the length of water trees formed in 24 hours. Relative rates of tree growth were calculated as heretofore described by equations (1) to (7). The data are summarized in Table I.
Example I was exactly repeated except that after compounding the composition was placed in a vacuum oven at 75°C for 48 hours. WTGR is listed in Table I.
Compositions were prepared according to Procedure A by compounding in a laboratory Brabender mixer: The polyethylene homopolymer and antioxidant of Control A and organo silane. The organo silane additives were formed in situ as in Example I. Relative rates of water tree growth were calculat ed as heretofore described in equations (1) to (7). The reactants used to produce the organo silane, as well as the concentrations and the WTGR are as set forth in Table I.
This Example illustrates the formation of the organo silane by prereacting a ketone with an aminosilane and adding this reaction product to the polymer.
The organo silane was prepared by reacting acetophenone and γ-aminotriethoxy silane in the presence of ammonium chloride catalyst. /
1.5 weight percent of the organo silane so prepared was added to the polyethylene of Control A in a laboratory Banbury mixer according to Procedure A. The WTGR after placing the composition in a vacuum oven at 75°C for 48 hours was 0.21.
This Example shows that heating under a vacuum does not reduce water treeing resistance as shown by the low value for WTGR.
The data in Table I shows that water tree growth rate was lower in all cases than that of Control A. In those Examples (2 and 6) where vacuum treatment was applied to the sample, the resistance to water treeing was retained, as shown by the low value for WTGR.
Compositions were prepared according to Procedure A by compounding in a laboratory Brabender mixer or Banbury mixer: The polyethylene copolymer and antioxidant of Control B and organo silane.
The organo silane additives were formed in situ as in Example 1. Relative rates of water tree growth were calculatl ed as heretofore described in equations (1) to (7). The reactants used to produce the organo silane, as well as the concentration and the WTGR are as set forth in Table II.
Example 6 was exactly repeated except that the reactants used to prepare the organo silane, amount of such a prepared organo silane which was added to the polyethylene copolymer and WTGR are as set forth in Table III.
The data in Tables II and III show that the WTGR was appreciably lower in these Examples, as compared with that of Control B in which the value of WTGR is high. Also, this inhibition is retained by the composition, as seen by the low values of WTGR for the compositions of Examples 7, 10, 1 and 20, which were treated in a vacuum oven after make up.
| 标题 | 发布/更新时间 | 阅读量 |
|---|---|---|
| 一种调光膜用ITO导电膜的防电击穿制备方法 | 2020-05-08 | 392 |
| TSV结构电击穿寿命测试方法、装置、系统和控制设备 | 2020-05-13 | 517 |
| 排出燃料电池残留电能的装置和方法 | 2020-05-14 | 989 |
| 一种实验室用于高压控制的小型自动化机械开关装置 | 2020-05-08 | 104 |
| 一种疏水高介电聚丙烯平壁增强电力IFB波纹管及其制备方法 | 2020-05-12 | 579 |
| 一种钛酸铋钠基固态相变制冷材料及应用 | 2020-05-15 | 540 |
| 一种低剖面RFID测温标签 | 2020-05-11 | 431 |
| 一种应用于氧化扩散炉上的碳化硅管监测保护装置 | 2020-05-12 | 192 |
| 用于高真空室和高气压室转接的高电压电极法兰 | 2020-05-13 | 857 |
| 一种采煤机主控器 | 2020-05-13 | 542 |
高效检索全球专利专利汇是专利免费检索,专利查询,专利分析-国家发明专利查询检索分析平台，是提供专利分析，专利查询，专利检索等数据服务功能的知识产权数据服务商。
我们的产品包含105个国家的1.26亿组数据，免费查、免费专利分析。
专利汇分析报告产品可以对行业情报数据进行梳理分析，涉及维度包括行业专利基本状况分析、地域分析、技术分析、发明人分析、申请人分析、专利权人分析、失效分析、核心专利分析、法律分析、研发重点分析、企业专利处境分析、技术处境分析、专利寿命分析、企业定位分析、引证分析等超过60个分析角度，系统通过AI智能系统对图表进行解读，只需1分钟，一键生成行业专利分析报告。