Raw mix for the production of portland cement clinker
专利汇可以提供Raw mix for the production of portland cement clinker专利检索，专利查询，专利分析的服务。并且A raw mix for the production of portland cement mix consists of a lime component, a clay component, an iron-containing component, and a modifying additive comprising hydrolysis and yeast production waste liquors and products of neutralization of chlorine-containing off-gas from titanium and magnesium production, with the following proportioning of the components (% by weight):______________________________________ lime component 50-52 clay component 7.5-10 iron-containing component 1-1.5 hydrolysis and yeast production waste liquors 30-38 products of neutralization of chlorine- containing off-gas from titanium and magnesium production 1-9. ______________________________________ The raw mix according to the invention exhibits improved physico-chemical and mechanical properties. Fluidity of the mix is from 58 to 60 mm, the degree of decarbonization is as high as 18%. Clinker prepared from the mix according to the invention has a strength of from 550 to 560 kgf/cm.sup.2, and the roasting temperature is 80.degree.-140.degree. C. lower.，下面是Raw mix for the production of portland cement clinker专利的具体信息内容。
We claim:1. A raw mix composition for the production of portland cement clinker, consisting of a lime component, a clay component, an iron-containing component, and a modifying additive which comprises hydrolysis and yeast production waste liquors and products of neutralization of chlorine-containing off-gas from titanium and magnesium production, with the following proportions of components (% by weight):______________________________________ lime component 50-52 clay component 7.5-10 iron-containing component 1-1.5 hydrolysis and yeast production waste liquors 30-38 products of neutralization of chlorine- containing off-gas from titanium and magnesium production 1-9. ______________________________________ 2. The raw mix composition of claim 1, wherein the lime component is selected from the group consisting of limestone, chalk, and marl.3. The raw mix composition of claim 1, wherein the iron-containing component is selected from the group consisting of pyrite cinder and ore dust.
The invention relates to raw mixes for the production of portland cement clinker.
FIELD OF THE ART
Such clinker is widely used in the manufacture of highgrade cements.
Basic starting materials for the production of portland cement clinker include lime and clay components, and various adjusting additives.
The additives are used as means for adjusting the properties of the raw mix, clinker and cement.
The knowledge of the mechanism of additives and their influence on the mechanical properties of clinker enables a diversification of properties of raw mixes and production of clinker exhibiting a complex of predetermined useful properties.
Thus, it is known to use such modifying additives as CaCl2, TiO2 and the like. These additives improve certain properties of a raw mix, such as plasticity and strength performance of clinker. They are, however, in a short supply and expensive. From the economical viewpoint, it is expedient to use production wastes as additives.
BACKGROUND OF THE INVENTION
Known in the art is a raw mix for the production of portland cement clinker, containing lime and clay components. The composition of this mix also includes an iron-containing component (cinder)--waste from chemical production, and a manganese concentrate for an adjustment of alumina and siliceous indexes. As modifying additives for such mixes, the use is made of e.g. blast-furnace dust which is the waste of blast-furnace metal production, waste of soda production containing up to 70% of CaCl2.
These raw mixes are widely used. These mixes are used for the production of high-grade clinker. The introduction of additives improves the degree of mineralization, and intensifies the roasting process.
No one additives used can, however, impart to the raw mix and resultant clinker a complex of useful properties.
Known in the art is a raw mix for the production of portland cement clinker containing carbonate, clay and iron-containing components, and oxygen-containing chlorine compounds as a modifying additive with the following proportioning of the components (% by weight):
______________________________________lime component 70-82clay component 15-19Pelletized secondary lead-zincslag 3-10oxygen-containing chlorinecompound 1-2______________________________________
As oxygen-containing chlorine compounds, use is made of oxidizers: calcium chlorine, hypochlorite, and chlorate.
This raw mix exhibits a complex of useful properties and, moreover, the use of the above-mentioned additives enables a lowering of the roasting temperature in the process of the clinker production. The additive used cannot, however, ensure desired fluidity of a mix, required moisture content and adequate degree of decarbonization.
Clinker produced from this mix exhibits low strength.
SUMMARY OF THE INVENTION
It is an object of the invention to provide a raw mix which exhibits valuable properties; such as improved fluidity with minimum required moisture content, as well as an improved degree of mineralization.
In accordance with this and other objects, the invention resides in a mix containing a lime component, a clay component, an iron-containing component, and a modifying additive. According to the invention, the modifying component comprises hydrolysis and yeast production waste liquors and products of neutralization of chlorine-containing off-gas of titanium-magnesium production, with the following proportion of the components (% by weight):
______________________________________lime component 50-52clay component 7.5-10iron-containing component 1-1.5hydrolysis and yeast production wasteliquors 30-38products of neutralization of chlorine-containing off-gas from titanium-man-ganese manufacture 1-9______________________________________
As the lime component, use may be made of, e.g. limestone, chalk, marl. As the clay component use may be made of various clays and loams. As the iron-containing component use may be made of pyrite cinder, ore dust.
As mentioned above, the modifying additive is made of hydrolysis and yeast production waste liquors and products of neutralization of chlorine-containing off-gas from titanium-magnesium production.
Hydrolysis and yeast production waste liquors are the wastes of yeast production plants, and have the following chemical composition (% by weight):
______________________________________organic compounds 50-54ammonium nitrogen 5-7H2 CO3 2-3P2 O5 1-1.5Mg 1-2K 0.3-0.8Clact. 1-2Ca 2-3Na 0.3-0.8SO4 5-7water the balance to 100.______________________________________
Products of neutralization of chlorine-containing off-gas of titanium-magnesium production comprise a 60-80% solution having the following chemical composition (% by weight):
______________________________________CaO 15.8-31.2 Ca(C10)2 5-5.8CaCl2 12.5-16.2 CaCO3 1.7-2.5Clact. 9.5-17.1 C 2-6.0TiO2 10.0-13.0 FeO 2.0-10.0Al2 O3 7.04-10.0 SiO2 7.0-30.0MgO 5.0-9.0 Mn 0.2-0.3V2 O5 0.1-0.4 Cr2 O3 0.3-0.8S 0.9-1.5 water the balance to 100.______________________________________
Content of chlorine up to 15-17% in the products of neutralization of chlorine-containing off-gas from titanium-magnesium production improves the degree of decarbonization of the raw mix at the stage of preparation of coarse sludge by 15-20%.
The presence of chlorine contributes also to the decomposition of organic compounds of hydrolysis and yeast production waste liquors. As a result, the fluidity of the mix increases by 3-5%. Moreover, owing to the presence of chlorine, calcium chloride is formed to intensify the roasting process.
The presence of other components in the products of neutralization of chlorine-containing off-gas has a positive effect on the properties of both raw mix and clinker. Thus Al2 O3 contributes to the improvement of reactivity of the mix as it is present in the form of a free oxide. This results in improved strength characteristics of clinker.
The raw mix for the production of portland cement clinker according to the invention exhibits improved physicochemical and mechanical properties. Thus the fluidity of the mix is from 50 to 60 mm which is 3 to 5 mm better compared to the raw mix containing oxygen-containing chlorine compounds as an additive; the degree of decarbonization is also considerably improved (up to 12-18%).
Clinker produced from the raw mix according to the invention has an improved strength from 550 to 560 kgf/cm2, the roasting temperature is lowered by 80°-140° C., the kiln output is improved by 2-3% and fuel consumption is reduced by 3-4%.
DETAILED DESCRIPTION OF THE INVENTION
The process for the preparation of a raw mix for the production of portland cement clinker is carried out as follows.
A lime component is preliminarily crushed in two stages: first, in a jaw breaker and than in a hammer mill. Then the comminuted lime component and a clay component are charged in a pre-set ratio into a rod mill, into which is also fed hydrolysis and yeast production waste liquors and products of neutralization of chlorine-containing off-gas of titanium and magnesium production. The resultant comminuted sludge is fed from the rod mill into a coarse sludge basin. The sludge is analyzed to determine the content of CaCO3, Al2 O3, Fe2 O3, SiO2 and Cl. The sludge is pumped from the basin into a ball mill, into which is also fed an iron-containing component. They are finely ground together.
For better understanding of the invention, specific examples are given below.
EXAMPLE 1
A raw mix for the production of portland cement clinker of the following composition (% by weight) was prepared:
______________________________________limestone 50clay 10ore dust 1hydrolysis and yeast productionwaste liquors 38products of neutralization ofchlorine-containing off-gasfrom titanium and magnesiumproduction 1______________________________________
Limestone was first comminuted in a jaw breaker and then, in a hammer mill. Clay and comminuted limestone were charged into a rod mill, to which were also fed hydrolysis and yeast production waste liquors and products of neutralization of chlorine-containing off-gas from titanium and magnesium production. The resultant comminuted sludge was fed to a coarse sludge basin and therefrom, to fine grinding ball mills to be comminuted together with ore dust to a pre-set fineness.
The resultant raw mix had the following properties:
______________________________________fluidity 58 mmmoisture capacity 39%.______________________________________
In the production of clinker from this mix, the temperature at which the clinker formation process was completed was lowered from 1500° C. to 1420° C. The strength of clinker produced using this raw mix was 550 kgf/cm2.
EXAMPLE 2
A raw mix for the production of portland cement clinker of the following composition (% by weight) was prepared:
______________________________________limestone 51clay 8.5pyrite cinder 1.0hydrolysis and yeast productionwaste liquors 35.0products of neutralization ofchlorine-containing off-gas fromtitanium and magnesium pro-duction 4.5.______________________________________
The mix was prepared as described in Example 1.
______________________________________fluidity 59 mmmoisture capacity 38.5%.______________________________________
In the production of clinker using this raw mix, the temperature at which the clinker formation process was completed was lowered from 1500° C. to 1390° C., the strength of clinker produced from this raw mix was 555 kgf/cm2.
EXAMPLE 3
A raw mix for the production of portland cement clinker having the following composition (% by weight) was prepared:
______________________________________limestone 52clay 7.5pyrite cinder 1.5hydrolysis and yeast production wasteliquors 30products of neutralization of chlorine-containing off-gas from titanium andmagnesium production 9.0______________________________________
The mix was prepared as described in Example 1. The resultant raw mix had the following properties:
______________________________________fluidity 60 mmmoisture capacity 39%______________________________________
In the production of clinker using this raw mix, the temperature at which the clinker formation process was completed was lowered from 1500° C. to 1360° C., the strength of clinker produced from this raw mix was 565 kgf/cm2.
| 标题 | 发布/更新时间 | 阅读量 |
|---|---|---|
| 一种PPR聚氨酯发泡保温管热力给水系统的施工方法 | 2020-05-11 | 574 |
| 一种利用铁尾矿生产聚合硫酸铝铁净水剂和硅胶的方法 | 2020-05-11 | 672 |
| 一种轻质建筑陶粒及其制备方法 | 2020-05-12 | 81 |
| 一种石灰立窑阶梯式旋转布料系统及布料方法 | 2020-05-11 | 704 |
| 以工业废弃物为主要原料制备的陶粒及其制备方法 | 2020-05-11 | 173 |
| 一种混凝土轻集料及其制备方法 | 2020-05-12 | 540 |
| 一种酸性废石膏综合处理与循环利用的工艺 | 2020-05-11 | 271 |
| 一种手持式生料带缠绕机 | 2020-05-08 | 57 |
| 一种彩色生料带生产用冷却装置 | 2020-05-08 | 35 |
| 一种新能源耐高温超软铝导体电缆 | 2020-05-11 | 192 |
高效检索全球专利专利汇是专利免费检索,专利查询,专利分析-国家发明专利查询检索分析平台，是提供专利分析，专利查询，专利检索等数据服务功能的知识产权数据服务商。
我们的产品包含105个国家的1.26亿组数据，免费查、免费专利分析。
专利汇分析报告产品可以对行业情报数据进行梳理分析，涉及维度包括行业专利基本状况分析、地域分析、技术分析、发明人分析、申请人分析、专利权人分析、失效分析、核心专利分析、法律分析、研发重点分析、企业专利处境分析、技术处境分析、专利寿命分析、企业定位分析、引证分析等超过60个分析角度，系统通过AI智能系统对图表进行解读，只需1分钟，一键生成行业专利分析报告。