Stent

The present invention relates to stents and, more particularly, to methods of fabricating and deploying stents.

The term "stent" has come into widespread use to denote any of a large variety of spring-like support structures, in the form of a tube which is open at both ends, which can be implanted inside a blood vessel or other tubular body conduit, to help keep the vessel or conduit open. Stents may be used following balloon angioplasty to prevent restenosis and may, more generally, be used in repairing any of a number of tubular body conduits, such as those in the vascular, biliary, genitourinary, gastrointestinal and respiratory systems, among others, which have narrowed, weakened, distorted, distended or otherwise deformed, typically as a result of any of a number of pathological conditions.

An effective stent must possess a number of important and very specific characteristics. Specifically, the stent should be chemically and biologically inert to its surroundings and should not react with, or otherwise stimulate, the living tissues around it. The stent must further be such that it will stay in the correct position and continue to support the tubular body conduit into which it is implanted over extended periods of time. Further, the stent must have the ability to return to its prescribed in-place diameter after the stent diameter has been significantly reduced prior to its insertion, usually tightly wrapped on a catheter, into the tubular body conduit.

These requirements limit the suitable metal stent materials to just a few metals and alloys. To date, it has been found that various alloys of nickel and titanium (hereinafter "nitinol"), with or without certain coatings, have the desired properties and are considered suitable for use in stent applications.

Specifically, nitinols, with or without special coatings, have been found to be chemically and biologically inert and to inhibit thrombus formation. Nitinols are, under certain conditions, also superelastic which allows them to withstand extensive deformation and still resume their original shape. Furthermore, nitinols possess shape memory, i.e., the metal "remembers" a specific shape fixed during a particular heat treatment and can resort to that shape under proper conditions. Shape-memory alloys can be formed into a predetermined shape at a suitable heat treatment temperature. At temperatures below the transition temperature range ("TTR") certain nitinol alloys are in their martensite phase wherein they are highly ductile and may be plastically deformed into any of a number of other shapes. The alloy returns to its austenite phase, returning to its original predetermined shape upon reheating to a temperature above the transition temperature range. The transition temperature varies with each specific combination ratio of the components in the alloy.

The superelasticity of nitinols and their shape memory characteristics makes it possible to fabricate a stent having the desired shape and dimensions. Once formed, the stent can be temporarily deformed into a much narrower shape for insertion into the body. Once in place, the stent can be made to resume its desired shape and dimensions. Certain alloys of nickel and titanium can be made which are plastic at temperatures below about 30°C and are elastic at body temperatures, above 35°C. Such alloys are widely used for the production of stents for medical use since these nitinols are able to resume their desired shape at normal body temperature without the need to artificially heat the stent.

While such stents have been proven effective, they continue to suffer from a number of disadvantages. First, there is, in certain cases, a tendency for tissue to grow in the gaps between adjoining loops of the stent. Over time, such growth could lead to the constriction, or even the complete closure, of the tubular body conduit in which the stent was introduced in order to keep open. A continuous, gap-free, tube structure with no gaps would eliminate such undesired tissue growth. However, a rigid tube would lack the highly desirable flexibility which a coiled spring configuration offers.

Another disadvantage is that the techniques for locating stents in a body conduit are such that the stents are often installed at a location which is not precisely the intended optimal location.

There is thus a widely recognized need for, and it would be highly advantageous to have, a stent which would be suitably flexible but which would significantly reduce, or even eliminate, the possibility of undesired tissue growth between the coils of the stent.

There is further a widely recognized need for, and it would also be highly advantageous to have, a technique for installing stents which would allow the stent to be located at precisely the desired location, either by controlling the stent design or by devising adequate methods for its accurate release. Furthermore, in those cases where the "shape memory" characteristic is used and the stent is to be heated in its final location in the body to cause it to resume its memorized shape, it is desired and advantageous to have a way of heating the stent which significantly reduces, or even eliminates, the chance of damaging surrounding tissue through heating which is conducted for too long and/or at temperatures which are too high.

According to the present invention there is provided a stent comprising a coiled wire which is configured for being immobilized on a catheter at a plurality of points on the coiled wire, the points being selectively releasable from the catheter such than, during deployment of the stent, at least one of the points is releasable prior to at least one other of the points.

Preferably the stent is formed of shape memory alloy, such as nitinol. Preferably the coiled wire includes at least one section which is wound in one sense and at least one section which is wound in the opposite sense, deployment of said stent taking place by tightly winding the stent onto a catheter and subsequently allowing the stent to resume its normal dimensions.

Some embodiments according to the present invention enable use of a method of deploying a stent in a desired location, comprising: (a) tightly winding the stent onto a catheter; (b) immobilizing at least two tie-down points on the stent using a disconnectable thread; (c) bringing the stent to the desired location where the stent is to be deployed; (d) causing the thread to disconnect at one or more of the tie-down points, thereby releasing the tie-down point, wherein said disconnectable thread is meltable and said thread is disconnected by heating the thread so as to cause the thread to melt.

The present invention offers stents and associated deployment techniques which make it possible to accurately install the stent in a specific location of a body tubular conduit.

The invention is herein described, by way of example only, with reference to the accompanying drawings, wherein:

• FIG. 1 is a perspective view of a stent wound and immobilized on a catheter, according to the prior art;
• FIG. 2 is a close-up side cross sectional view of a portion of the system of Figure 1;
• FIG. 3 is a perspective view of one embodiment of a stent according to the present invention showing two oppositely wound sections;
• FIG. 4 is a schematic side view of the stent of Figure 3 with reference to a catheter on which the stent is delivered to its desired location after release of the intermediate point;
• FIG. 5 is a schematic side view of the stent of Figure 3 when would tightly on a catheter on which the stent is delivered to its desired location;
• FIG. 6 is a side view of a catheter such as might be used in Figure 5;
• FIG. 7 is a side view of the catheter of Figure 6 with the stent would on the catheter;
• FIG. 8 is a side view of the expanded stent after its release;
• FIG. 9 is a perspective view of another embodiment of a stent according to the present invention showing a plurality of oppositely wound sections;
• FIG. 10 is a schematic side view of the stent of Figure 9 with reference to a catheter on which the stent is delivered to its desired location with the stent partly released;
• FIG. 11 is a schematic side view of the stent of Figure 9 when wound tightly on a catheter on which the stent is delivered to its desired location;
• FIG. 12 is a perspective view of the embodiment of Figures 9-11 showing one method of immobilizing the stent;
• FIG. 13 is a close-up perspective cross sectional view of one portion of the system of Figure 12 showing a tie-down of an intermediate point;
• FIG. 14 is a close-up perspective cross sectional view of one portion of the system of Figure 12 showing a tie-down of an end point;
• FIG. 15 is a perspective view of a variation of the embodiment of Figure 9, showing a stent wherein the immobilization is effected in somewhat different fashion;
• FIG. 15A is a side view of a catheter such as might be used in Figure 15;
• FIG. 15B is a side view of the catheter of Figure 15A with the stent wound on the catheter;
• FIG. 15C is a side view of the expanded stent as it would appear after it has been released from the catheter;
• FIG. 16 is a side cross sectional view of another embodiment of a stent according to the present invention when tightly wound about a catheter (not shown);
• FIG. 17 is a side cross sectional view of the embodiment of Figure 16 when unwound for deployment;
• FIG. 18 is a schematic cross sectional side view of a catheter showing one embodiment of a technique for releasing the stent (not shown) using a single electrical circuit;
• FIG. 19 is as in Figure 18 except that two electrical circuits are used to provide for the sequential release of various points of the stent.

In many applications, it is important to precisely control the flexibility of the stent as well as the interloop spacing and tightness. A number of factors must be considered in selecting the proper flexibility and interloop spacing. First, the stent must be sufficiently flexible to follow the natural shape and dimensions of the body conduit into which it is installed without undue stress. The stent must also be sufficiently flexible to adequately follow the various movements of the conduit. These requirements tend to indicate that a coiled, or spring-like, structure be used.

However, the stent must not be too loose since this may erode its body conduit support function and since when the stent loosens significant interloop gaps are formed which tend to encourage the growth of surrounding tissue into the separations. Such ingrowth may have serious adverse consequences.

A stent is typically made by first tightly winding a wire of a suitable material, such as nitinol, on a mandrel. The assembly is then heated to a suitable temperature so as to impart to the stent its desired shape.

Conventional stents must be accurately placed in a specific location in the body conduit in order to be most effective. A common placement technique currently used is illustrated in Figures 1 and 2. Stent 20 is tightly wound around a catheter 24, which typically features helical grooves 26 sized and shaped to accommodate stent 20 in its tightly wound configuration.

The two ends of stent 20 are typically bubbled, i.e. the ends feature a slightly enlarged diameter. Each end of stent 20 is immobilized by a thread 28 which is anchored by wrapping around catheter 24 several times. Thread 28 is wrapped over the end of stent 20 as shown in Figure 2. Catheter 24 features a small diameter bore 30 through which runs a release wire 32. Portions of thread 28 enter transversely into bore 30 near the bulbed end of stent 20 and thread is connected with release wire 32 (see Figure 2) so that as long as release wire 32 is in placed thread 28 immobilizes the end of stent 20. When both ends of stent 20 are so immobilized, stent 20 is effectively prevented from unwinding and resuming its preset shape.

To deploy stent 20 in the body, catheter 24 is first brought to the appropriate position. Release wire 32 is then pulled, thereby releasing the ends of stent 20. Stent 20 then immediately proceeds to unwind, enlarge and install itself into the body tubular conduit while getting shorter in proportion to the diameter growth, as is the case for a stent having adjoining loops which contact each other. However, in the process of unwinding, stent 20 assumes a final position which is somewhat arbitrary, within its original length, and which depends, to some extent, on the local resistance encountered to the unwinding in the uneven blood vessel. The lack of certainty in the accurate placement of the stent often degrades its effectiveness. Hence, it is quite important to be able to release the stent with a high degree of accuracy.

Furthermore, the unwinding action of a stent of conventional design is accompanied by the rapid turning through many cycles of the stent coils. Such a turning could have a detrimental effect on surrounding tissue since the rapid and prolonged turning could abrade or otherwise damage the interior walls of body vessels in which the stent is released.

Accordingly, a stent according to one embodiment of the present invention is made up of a coiled wire which is characterized in that the wire includes at least one section which is wound in one sense and at least one section which is wound in the opposite sense. Preferably, the stent includes two sections with each of these sections representing substantially one half of the stent. An example of such a stent is shown in Figures 3-8.

Stent 120 has a central point 40 where the winding direction changes, and two end points 42. To place stent 120 in a body conduit, stent 120 is first tightly wound onto catheter 24 and end points 42 are immobilized using release wire 32 as described above in the context of Figures 4 and 5, or in any other suitable manner. In addition, central point 40 is also immobilized in a similar manner, but using a second release wire 33.

To place stent 120, catheter 24 is first brought to the proper location. Next, central point 40 is released by using second release wire 33. This allows stent 120 to unwind without any axial displacement, since the two ends 42 are still immobilized. As stent 120 unwinds it assumes its full diameter and is firmly installed onto the inner walls of the body tubular conduit.

At this point the two end points 42 are released by using release wire 32, freeing stent 120 from catheter 24, and allowing the latter to be withdrawn. Since stent 120 is already fully unwound and firmly implanted in the body conduit prior to the release of end points 42, stent 120 does not move upon the release of end points 42 and remains firmly installed in the correct position. Shown in Figures 8A, 8B and 8C are more detailed views of catheter 24 and stent 120 as they might appear in an actual application.

In another embodiment of stents according to the present invention showing in Figures 9-12, stent 220 is made up of several sections with adjoining sections wound in opposite directions. Preferably, adjoining loops of stent 220 are wound in opposite directions, with intermediate points 140 representing the regions where winding directions change. To make such a stent, a catheter can be used which features a series of suitably placed pins or protrusions. The wire is wound about the mandrel and use is made of the pins or protrusions to wrap the wire around these in order to reverse the winding direction.

Shown in Figure 12 is one scheme for attaching stent 220 to catheter 24. Here a first release wire 132 immobilizes the two end points 42 and approximately one half of intermediate points 140, while a second release wire 133 serves to immobilize the balance of intermediate points 140. Each of release wires 132 and 133 is preferably located in its own bore, 232 and 233, respectively. The release of such a stent is not accompanied by the rapid and prolonged turning of the coils of the stent but is, rather, achieved by minimum and uniform turning of the coils through approximately two turns before the stent is fully deployed in the body vessel.

Figures 13 and 14 depict possibilities for the actual immobilization of an intermediate point 140 and an end point 42, respectively.

Another embodiment of a stent according to the present invention is shown in Figure 15, where at the end points and in the vicinity of each winding direction change, stent 320 features a kink or depression 50 in the otherwise circular cross section of the stent. The kink or depression 50 allows stent 320 to be immobilized on a catheter (not shown) by inserting a release wire (not shown) above kink or depression 50 (see Figure 15).

As can be better seen in Figures 15A and 15B, catheter 24 preferably features slots 25 which accommodate the kinked portions of stent 320 so that release wires 32 and 33 can pass on the outside of the kinked portions and serve to immobilizes stent 320. Figure 15C shows stent 320 as it would appear after release from catheter 24.

Other variations and improvements of methods of immobilizing and releasing stents, whether conventional, or those according to the present invention, may be envisioned.

When a stent is to be inserted deep into the body, the catheter used in deploying the stent is necessarily very long and may need to follow a highly convoluted path on its way to the desired deployment location. If the stent is to be released from the catheter by pulling on the release wire, the friction between the release wire and its bore may be sufficiently high that pulling the release wire will result in the deformation of the entire catheter and bring about the displacement of the catheter tip on which the stent is wound. This, in turn, could result in the improper placement of the stent.

One way of avoiding this difficulty is demonstrated in Figures 18 and 19. Here the release wire is an electrically conducting wire which, unlike the release wires described above, is not movable but is, rather, used to conduct a small electric current upon activation by the operator. In Figure 18, a pair of threads 28 are shown, each of which is used to immobilize a certain point on the stent (not shown). Thread 28 is in contact with a heat producing element 60 which forms a part of the electrical circuit Heat producing element 60 may be a resistor which converts electrical energy into heat. Thread 28 is made of a material such that when heat producing element 60 is activated, thread 28 is caused to melt thereby releasing the stent.

In the embodiment of Figure 19 catheter 24 features two circuits, rather than one. This makes it possible to sequentially release various points of the stent, for example, as described above. As will readily be appreciated, the basic concept can be used in a variety of related ways. For example, thread 28 can be caused to break or disconnect by cutting, by chemical reaction, and the like.

In some cases it is desirable that the stent form a continuous wall. This may be accomplished by encasing the wire making up the stent in a thin plastic envelope which will provide the continuous wall when the stent is in position.

In the embodiment shown in Figures 16 and 17 a metal core 80, preferably made of nitinol, is encased in a shaped envelope 82, preferably of a suitable plastic, which allows the stent to be tightly wound on the catheter and which forms a continuous surface when the stent is unwound. The envelope is not continuous and does not directly connect adjoining coils. Rather, the wire making up the stent is enveloped in a suitable material, such as plastic, which features an extension such that, when deployed, the extension serves to bridge the gap between adjoining coils of the stent.

The configuration shown in Figures 16 and 17 is such that when the stent expands and its metal core loops are separated from each other (Figure 17) the stent retains its continuous sealed wall. Thus, a stent is obtained which features continuous walls and which is substantially the same length when wound onto the catheter for delivery and placement as when fully deployed in the body vessel. It should be noted that such a configuration may be useful even without reversing of the winding direction, since a sealed wall is maintained even when adjoining loops are not completely contiguous.

It is to be noted that a stent according to the present invention, especially one featuring a continuous wall supported on a metal coil frame, as described above, is highly desirable in that such a structure is able to support the body vessel and prevent tissue ingrowth without undue interference with the normal flow of blood and other bodily fluids.