161 |
REDUCED VOC TIRE CEMENT |
US15769878 |
2016-10-13 |
US20180312732A1 |
2018-11-01 |
Ross W. Widenor; Amy M. Randall |
Disclosed herein are adhesive compositions comprising at least one conjugated diene-containing polymer or copolymers, including natural rubber, and a liquid terpene-based solvent, wherein the adhesive composition is essentially free of petroleum-based solvents and petroleum-based resins. Also disclosed are curable adhesive composition embodiments further comprising a cure package. A related process for adhering two tire components together using a curable adhesive composition is also disclosed as is a tire comprising two components adhered by a specified process including use of a curable adhesive composition. |
162 |
Process for binding substrates with a liquid optically clear photo-curable adhesive |
US14550431 |
2014-11-21 |
US10093837B2 |
2018-10-09 |
Daoqiang Lu; Masao Kanari; Junichi Sawanobori |
A process for binding a top substrate to a base substrate is disclosed, in which (a) a liquid optically clear photo-curable adhesive is applied onto the top side of the base substrate, (b) the liquid optically clear photo-curable adhesive is partially cured by exposure to electromagnetic radiation comprising a wavelength ranging from 200 nm to 700 nm, (c) the top substrate is attached on the partially cured adhesive layer of step (b), (d) the adhesive is fully cured by exposure to electromagnetic radiation comprising a wavelength ranging from 200 nm to 700 nm. |
163 |
Adhesive bonding composition and method of use |
US15126834 |
2015-03-18 |
US10087343B2 |
2018-10-02 |
Zakaryae Fathi; Frederic Avery Bourke, Jr.; Harold Walder |
A method of and system for adhesive bonding. The method and system a) treat a surface of an element to be bonded to provide an adherent structure including one or more rubber compounds on the surface; b) place a polymerizable adhesive composition, including at least one photoinitiator and at least one energy converting material, in contact with the adherent structure and two or more components to be bonded to form an assembly, c) irradiated the assembly with radiation at a first wavelength, capable of conversion by the at least one energy converting material, to a second wavelength capable of activating the at least one photoinitiator to produce from the polymerizable adhesive composition a cured adhesive composition; and d) adhesively join the two or more components by way of the adherent structure and the cured adhesive composition. |
164 |
METHODS FOR RETREADING TIRES EMPLOYING CUSHION GUM WITH STABLE DINITRILE OXIDE CURE SYSTEM |
US15753762 |
2016-08-22 |
US20180244007A1 |
2018-08-30 |
Robert Barned; Joshua Abell; David Bender |
A process for retreading a tire, the process comprising the steps of providing a tire casing, providing a cured rubber component having first and second planar surfaces, providing a cushion gum, wherein the cushion gum contains a cure system comprising at least one stable aryl dinitrile oxide compound, applying the cushion gum to the tire casing, and forming a tire composite by applying the second planar surface of the cured rubber component to the cushion gum. |
165 |
ADHESIVE COMPOSITION, ADHESIVE FILM COMPRISING SAME, AND ORGANIC ELECTRONIC DEVICE COMPRISING SAME |
US15580193 |
2016-06-09 |
US20180171188A1 |
2018-06-21 |
Kyung Yul BAE; Yoon Gyung CHO; Hyun Jee YOO; Se Woo YANG |
The present application relates to an adhesive composition comprising a curable oligomer and a polymer derived from butylene, an adhesive film comprising same, an organic electronic device comprising same, and a lighting apparatus and a display device comprising same. The adhesive film comprising the adhesive composition shows excellent moisture-blocking properties and enables an organic electronic device to have flexibility as well as excellent and reliable durability at high temperature and high humidity. |
166 |
RESIN COMPOSITION AND DISPLAY UNIT |
US15857018 |
2017-12-28 |
US20180143484A1 |
2018-05-24 |
Yoshihisa SHINYA; Yusuke KAMATA |
A display unit that includes an image display part and a light-transmitting protective part arranged on the image display part. A cured resin layer is arranged between the display part and the protective part. The cured resin layer has a transmittance of 90% or higher in the visible range and a storage modulus at 25° C. of 1×107 Pa or less. The cured resin layer is formed from a resin composition that has a cure shrinkage of 5% or less. |
167 |
Aqueous emulsion and adhesive in which same is used |
US15537996 |
2015-12-24 |
US09963520B2 |
2018-05-08 |
Hideki Maki; Masato Nakamae |
The present invention relates to an aqueous emulsion including an ethylenically unsaturated monomer unit-containing polymer as a dispersoid and a polyvinyl alcohol as a dispersant. The content of a free polyvinyl alcohol in the aqueous emulsion is 0.2 to 20 parts by mass relative to 100 parts by mass of the ethylenically unsaturated monomer unit-containing polymer. The free polyvinyl alcohol has a degree of saponification of 80.0 to 99.5 mol % and a viscosity-average degree of polymerization of 200 to 5000, and the free polyvinyl alcohol has a symmetry factor (W0.05h/2f) that satisfies the following expression (1) as determined by gradient high-performance liquid chromatography for reversed-phase separation using a water-acetone eluent according to JIS K 0124 (2011). 0.85≤W0.05h/2f≤1.30 (1) (The definitions of the symbols are omitted.) |
168 |
Aqueous adhesive composition for the bonding of wood |
US14763375 |
2014-01-28 |
US09938434B2 |
2018-04-10 |
David Doisneau |
An aqueous adhesive composition comprises a phenol/aldehyde resin and less than 16% by weight of unsaturated diene elastomer latex. The phenol/aldehyde resin is based on an aromatic polyaldehyde bearing at least two aldehyde functional groups and comprising at least one aromatic nucleus, and on a polyphenol comprising one or more aromatic nuclei. If just one aromatic nucleus is present, the latter bears two or three hydroxyl functional groups in the meta position with respect to one another and the remainder of the aromatic nucleus is unsubstituted. If several aromatic nuclei are present, at least two of them each bear two or three hydroxyl functional groups in the meta position with respect to one another, it being understood that the two positions ortho to at least one of these hydroxyl functional groups are unsubstituted. |
169 |
SILANE-MODIFIED COPOLYMER, MAKING METHOD, AND ADHESION IMPROVER |
US15691252 |
2017-08-30 |
US20180066093A1 |
2018-03-08 |
Munenao HIROKAMI |
A silane-modified copolymer comprising constituent units of butadiene, constituent units having a hydrolyzable silyl group, and constituent units having acid anhydride functionality is low volatile because of its molecular weight. It may be synthesized from relatively inexpensive reactants. |
170 |
MODIFIED LIQUID DIENE RUBBER AND RESIN COMPOSITION CONTAINING MODIFIED LIQUID DIENE RUBBER |
US15538076 |
2015-12-22 |
US20180022835A1 |
2018-01-25 |
Satoshi MOTODA; Kei HIRATA |
There are provided a modified liquid diene rubber that can be used for a curable resin composition and a resin composition containing the modified liquid diene rubber. The curable resin composition containing the modified liquid diene rubber has a much higher curing rate than that in the related art, and the resulting cured product has excellent mechanical properties, transparency, and heat resistance. Produced are a modified liquid diene rubber and a resin composition containing the modified liquid diene rubber. The modified liquid diene rubber includes a modifying group (p) partly containing a (meth)acryloyl group therein and a monomer unit (a1) derived from a conjugated diene compound. A carbon-carbon double bond derived from the conjugated diene compound has a hydrogenation rate of 30 to 95 mol %, and the modifying group (p) has a functional group equivalent weight of 700 to 20,000 g/eq. |
171 |
Inner liner for pneumatic tire and method for producing the same |
US13513429 |
2010-11-30 |
US09873238B2 |
2018-01-23 |
Shinji Tai; Hiroshi Kawai; Satoshi Yamakoshi; Kouta Isoyama; Masao Hikasa; Yuwa Takahashi; Hideki Kitano; Tetsuo Amamoto; Takatsugu Tanaka |
Disclosed is an inner liner for a pneumatic tire, the inner liner including no less than 8 resin-layers, the resin-layer having a layer A constituted with a resin composition containing a gas barrier resin, and a layer B constituted with a resin composition containing an elastomer, at least one of the resin compositions included in the layer A and the layer B that are adjacent with each other containing a metal salt, the content of the metal salt being no less than 1 ppm and no greater than 10,000 ppm in terms of metal element equivalent, and an interlayer adhesive force between the layer A and the layer B being no less than 500 g/15 mm. The layer A and the layer B are preferably alternately laminated. |
172 |
ADHESIVE COMPOSITION AND ADHERED ROOFING SYSTEM PREPARED USING THE ADHESIVE COMPOSITION |
US15629236 |
2017-06-21 |
US20180010021A1 |
2018-01-11 |
Wilfried CARL; Markus HAUFE |
The invention is directed to an adhesive composition including at least one rubber component, a solvent, and at least one powdered superabsorber polymer. The invention also relates to a method for bonding a roofing membrane to a substrate using the adhesive composition as a contact adhesive, to fully adhered membrane roofing system, and to the use of adhesive composition for adhering roofing membranes to substrates by contact bonding. |
173 |
AQUEOUS EMULSION AND ADHESIVE IN WHICH SAME IS USED |
US15537996 |
2015-12-24 |
US20170369601A1 |
2017-12-28 |
Hideki MAKI; Masato NAKAMAE |
The present invention relates to an aqueous emulsion including an ethylenically unsaturated monomer unit-containing polymer as a dispersoid and a polyvinyl alcohol as a dispersant. The content of a free polyvinyl alcohol in the aqueous emulsion is 0.2 to 20 parts by mass relative to 100 parts by mass of the ethylenically unsaturated monomer unit-containing polymer. The free polyvinyl alcohol has a degree of saponification of 80.0 to 99.5 mol % and a viscosity-average degree of polymerization of 200 to 5000, and the free polyvinyl alcohol has a symmetry factor (W0.05h/2f) that satisfies the following expression (1) as determined by gradient high-performance liquid chromatography for reversed-phase separation using a water-acetone eluent according to JIS K 0124 (2011). 0.85≦W0.05h/2f≦1.30 (1) (The definitions of the symbols are omitted.) |
174 |
Hot melt pressure-sensitive adhesive for labeling |
US14669630 |
2015-03-26 |
US09828535B2 |
2017-11-28 |
Makoto Takenaka; Tadashi Hayakawa |
The present invention provides a hot melt pressure-sensitive adhesive being highly environmentally-friendly, as well having sufficient adhesion, thermal stability and coating performance, and also having an excellent hand-peeling property and alkali-peeling property. The present invention relates to a hot melt pressure-sensitive adhesive for labeling comprising: (A) a polar functional group-modified conjugated diene-based polymer, (B) an aliphatic polyester-based resin, and (C) a tackifier resin. |
175 |
Pressure sensitive adhesive film and method of manufacturing organic electronic device using the same |
US14763410 |
2014-08-05 |
US09803112B2 |
2017-10-31 |
Hyun Jee Yoo; Suk Ky Chang; Yoon Gyung Cho; Kyung Yul Bae |
Provided are a pressure-sensitive adhesive film and a method of manufacturing an organic electronic device using the same. The pressure-sensitive adhesive film that may effectively block moisture or oxygen penetrated into an organic electronic device from an external environment, and exhibit reliability under harsh conditions such as high temperature and high humidity and excellent optical characteristics is provided. |
176 |
Acrylate-Terminated Urethane Polybutadienes From Low-Monomer 1:1 Monoadducts From Reactive Olefinic Compounds and Diisocyanates and Hydroxy-Terminated Polybutadienes for Liquid Optically Clear Adhesives (LOCAs) |
US15375225 |
2016-12-12 |
US20170174956A1 |
2017-06-22 |
Laura Ramon-Gimenez; Niko Haberkorn; Kai-Steffen Krannig; Nicolai Kolb; Hsin-Ho Wu; Juergen Steiger; Tung-Yi Sun |
The present invention relates to an optical clear resin and a method for producing a liquid optical clear photo-curable adhesive. |
177 |
WET OR DAMP SURFACE PREPARATION COMPOSITIONS |
US15301427 |
2015-04-01 |
US20170174903A1 |
2017-06-22 |
DAVID J. NEUDAHL; GREGG A. PATNODE; RANDALL S. TEARE; MICHAEL P. DANIELS |
The present application provides a primer composition, a method for treating a wet or damp surface with the primer composition, and a method to improve the adhesion of pavement markers to wet or damp surfaces. The primer composition comprises about 5 weight percent to about 90 weight percent of the reaction product of: (i) about 30 to about 70 parts by weight of an (meth)acrylate ester wherein the (meth)acrylate ester; (ii) about 70 to about 30 parts by weight of a hydrophilic acidic comonomer; and (iii) about 10 to about 100 parts based on 100 parts of the sum of the (meth)acrylate ester and the hydrophilic acid comonomer, of a plasticizer; dissolved in about 10 to about 95 weight percent of at least one organic solvent. |
178 |
STEEL REINFORCING ELEMENT COATED WITH AN ADHESIVE COMPOSITION CONTAINING AROMATIC ALDEHYDE AND POLYPHENOL |
US15116878 |
2015-02-05 |
US20170165942A1 |
2017-06-15 |
CLÉMENT MICHOUD; DAVID DOISNEAU |
The coated steel reinforcing element comprises one or more threadlike reinforcing elements, each comprising a steel core, and an adhesive layer coating at least a portion of the steel core of the or each threadlike reinforcing element. The coated steel reinforcing element is devoid of a metal layer between the steel core of the or each threadlike reinforcing element and the adhesive layer. The adhesive layer comprises an adhesive composition comprising at least one phenol/aldehyde resin based on at least: one aromatic aldehyde and one polyphenol comprising one or more aromatic nucleus/nuclei. |
179 |
SHEET TO BE PASTED ON ROAD SURFACE, FLOOR, OR WALL SURFACE AND SET FOR FORMING SHEET TO BE PASTED ON ROAD SURFACE, FLOOR, OR WALL SURFACE |
US15435304 |
2017-02-17 |
US20170158919A1 |
2017-06-08 |
Masahiko NORITSUNE; Toshiyuki KATAGIRI; Yoshihiko SANO |
An object of the invention is to provide a sheet for application to a road surface, a floor, or a wall surface of which following properties to a pasted road surface, a pasted floor, or a pasted wall surface are excellent, and of which strength is excellent and a set for forming a sheet for application to a road surface, a floor, or a wall surface, which can easily form the sheet.The sheet for application to a road surface, a floor, or a wall surface according to the invention has a pressure sensitive adhesive layer; a base material layer that is in contact with the pressure sensitive adhesive layer and of which a tensile elastic modulus is 150 MPa or less; and a protective layer of which a tensile elastic modulus is 1,000 MPa or greater, in this order. A set for forming a sheet for application to a road surface, a floor, or a wall surface according to the invention includes: an image forming sheet including a peeling layer, a pressure sensitive adhesive layer, a base material layer that is in contact with the pressure sensitive adhesive layer and of which a tensile elastic modulus is 150 MPa or less, and an image forming layer, in this order; and a protective sheet including a peeling layer, an adhesive layer, and a protective layer of which a tensile elastic modulus is 1,000 MPa or greater, in this order. |
180 |
ADHESIVE COMPOSITIONS, MANUFACTURE AND USE THEREOF |
US14781349 |
2014-04-07 |
US20170081571A1 |
2017-03-23 |
Andreas Lutz; Christof Braendli; Cathy Grossnickel |
The invention relates to an adhesive composition having an added component of rubber-epoxy such as XNBR-epoxy adducts. It was found that the new adhesive composition significantly reduces meander formation in the making of automotive parts. |