专利汇可以提供Potential pulse-scan methods of analyzing organic additives in plating baths with multi-component additives专利检索,专利查询,专利分析的服务。并且A cyclic voltammetric method for measuring the concentration of additives in a plating solution. The method generally includes providing the plating solution, having an unknown concentration of an additive to be measured therein and cycling the potential of an inert working electrode through a series of measurement steps. The series of measurement steps includes a metal stripping step including pulsing from an open circuit potential to a metal stripping potential between about 0.2 V and about 0.8 V, and holding the metal stripping potential until a corresponding current nears 0 mA/cm. The series of measurement steps further includes a cleaning step including pulsing from the metal stripping potential to a cleaning potential between about 1.2 V and about 1.6 V, and holding the cleaning potential for about 2 seconds to about 10 seconds. The series of measurement steps then includes a pre-plating step including pulsing from the cleaning potential to a pre-plating potential between about −0.2 V and about −0.5 V, and holding the pre-plating potential for about 2 seconds to about 10 seconds. The series of measurement steps additionally includes an equilibration step including pulsing from the pre-plating potential to the open circuit potential, and holding the open circuit potential for a predetermined time period, and a metal deposition step including scanning from the open circuit potential of the equilibration step to an additive sensitive potential, holding the additive sensitive potential for about 1 second to about 30 seconds, and scanning back to the open circuit potential. The method further includes plotting a profile of a deposition current resulting from the metal deposition potential as a function of time and integrating the deposition current to determine the concentration of the additive to be measured.,下面是Potential pulse-scan methods of analyzing organic additives in plating baths with multi-component additives专利的具体信息内容。
What is claimed is:1. A cyclic voltammetric method for measuring the concentration of additives in a plating solution, comprising:providing the plating solution, having an unknown concentration of an additive to be measured therein;cycling the potential of an inert working electrode through a series of measurement steps, comprising:a metal stripping step including pulsing from an open circuit potential to a metal stripping potential between about 0.2 V and about 0.8 V, and holding the metal stripping potential until a corresponding current is about 0 mA/cm;a cleaning step including pulsing from the metal stripping potential to a cleaning potential between about 1.2 V and about 1.6 V, and holding the cleaning potential for about 2 seconds to about 10 seconds;a pre-plating step including pulsing from the cleaning potential to a pre-plating potential between about −0.2 V and about −0.5 V, and holding the pre-plating potential for about 2 seconds to about 10 seconds;an equilibration step including pulsing from the pre-plating potential to the open circuit potential, and holding the open circuit potential for a predetermined time period; anda metal deposition step including scanning from the open circuit potential of the equilibration step to an additive sensitive potential, holding the additive sensitive potential for about 1 second to about 30 seconds, and scanning back to the open circuit potential; anddetermining a profile of a deposition current resulting from the metal deposition potential as a function of time and integrating the deposition current to determine the concentration of the additive to be measured.2. The method of claim 1, wherein the metal stripping step further comprises pulsing for about 2 seconds to about 10 seconds.3. The method of claim 1, wherein the metal stripping potential is between about 0.4 V to about 0.6 V.4. The method of claim 1, wherein the series of measurement steps is repeated until a steady state is reached.5. The method of claim 1, wherein the series of measurement steps is repeated from about 1 to about 5 times.6. The method of claim 4, wherein the profile of the deposition current when steady state has been reached are averaged to determine the concentration of the additive to be measured.7. The method of claim 1, wherein the equilibration step further comprises holding the open circuit potential for about 10 seconds to about 60 seconds.8. The method of claim 1, wherein the open circuit potential of the equilibration step is a stable open circuit potential.9. The method of claim 8, wherein the stable open circuit potential is held for about 5 seconds to about 10 seconds.10. The method of claim 1, wherein the metal deposition step further comprises scanning to an additive desorption potential and holding the desorption potential until substantially all of the additive desorbs from the working electrode surface, scanning to an additive adsorption potential and holding the adsorption potential for about 5 seconds to about 30 seconds, and scanning from the additive adsorption potential to the open circuit potential.11. The method of claim 10, wherein the additive desorption potential is held constant for about 1 second to about 30 seconds.12. The method of claim 1, further comprising integrating the deposition current over the additive sensitive potential range.13. A method for measuring the concentration of additives in a plating solution, comprising:cycling the potential of an inert working electrode through a series of measurement steps, comprising:a metal stripping step including pulsing from an open circuit potential to a metal stripping potential sufficient to remove substantially all metal on the working electrode, and holding the metal stripping potential until a corresponding current nears 0 mA/cm;a cleaning step including pulsing from the metal stripping potential to a cleaning potential, and holding the cleaning potential for about 2 seconds to about 10 seconds;a pre-plating step including pulsing from the cleaning potential to a pre-plating potential sufficient to plate a layer of metal on the working electrode, and holding the pre-plating potential for about 2 seconds to about 10 seconds;an equilibration step including pulsing from the pre-plating potential to the open circuit potential, and holding the open circuit potential for a predetermined time period; anda metal deposition step including scanning from the open circuit potential of the equilibration step to an additive sensitive potential, holding the additive sensitive potential for about 1 second to about 30 seconds, and scanning back to the open circuit potential; anddetermining a profile of a deposition current resulting from the metal deposition potential as a function of time and integrating the deposition current to determine the concentration of the additive to be measured.14. The method of claim 13, wherein the metal stripping step further includes pulsing to a metal stripping potential between about 0.2 V and about 0.8 V and holding the metal stripping potential for about 2 seconds to about 10 seconds.15. The method of claim 13, wherein the metal stripping step includes pulsing to a potential between about 0.4 V to about 0.6 V.16. The method of claim 13, wherein the cleaning potential is between about 1.2 V and about 1.6 V.17. The method of claim 13, wherein the pre-plating potential is between about −0.2 V and about −0.5 V.18. The method of claim 13, wherein the series of measurement steps is repeated until a steady state is reached.19. The method of claim 13, wherein the series of measurement steps is repeated from about 1 to about 5 times.20. The method of claim 19, wherein the profiles from the deposition charges when steady state has been reached are averaged to determine the concentration of the additive to be measured.21. The method of claim 13, wherein the equilibration step comprises leaving the potential at the open circuit potential for about 10 seconds to about 60 seconds.22. The method of claim 13, wherein the equilibration step comprises pulsing the potential to a stable open circuit potential for about 5 seconds to about 10 seconds.23. The method of claim 13, wherein the metal deposition step further comprises scanning to an additive desorption potential and holding the desorption potential until substantially all of the additive desorbs from the working electrode surface, scanning to an additive adsorption potential and holding the adsorption potential for about 5 seconds to about 30 seconds, and scanning from the additive adsorption potential to the open circuit potential.24. The method of claim 23, wherein the additive desorption potential is held for about 1 second to about 30 seconds.25. The method of claim 13, further comprising integrating the deposition current over the additive sensitive potential range.26. A cyclic voltammetric method for measuring the concentration of additives in a plating solution, comprising:cycling the potential of an inert working electrode through a series of measurement steps, comprising:a metal stripping step including pulsing from an open circuit potential to a metal stripping potential between about 0.4 V and about 0.6 V, and holding the metal stripping potential for about 2 seconds to about 10 seconds;a cleaning step including pulsing from the metal stripping potential to a cleaning potential between about 1.2 V and about 1.6 V, and holding the cleaning potential for about 2 seconds to about 10 seconds;a pre-plating step including pulsing from the cleaning potential to a pre-plating potential between about −0.2 V and about −0.5 V, and holding the pre-plating potential for about 2 seconds to about 10 seconds;an equilibration step including pulsing from the pre-plating potential to the open circuit potential, and holding the open circuit potential for about 10 seconds to about 60 seconds; anda metal deposition step including scanning from the open circuit potential of the equilibration step to an additive sensitive potential, holding the additive sensitive potential for about 1 second to about 30 seconds, and scanning back to the open circuit potential;repeating the series of measurement steps until a steady state is reached;determining a profile of a deposition current resulting from the metal deposition potential as a function of time and integrating the deposition current to determine the concentration of the additive to be measured; andaveraging the deposition currents from the series of measurement steps when steady state has been reached to determine the concentration of the additive to be measured.27. A cyclic voltammetric method for measuring the concentration of additives in a plating solution, comprising:providing the plating solution, having an unknown concentration of an additive to be measured therein;cycling the potential of an inert working electrode through a series of measurement steps, comprising:a metal stripping step including pulsing from an open circuit potential to a metal stripping potential between about 0.4 V and about 0.6 V, and holding the metal stripping potential for about 2 seconds to about 10 seconds;a cleaning step including pulsing from the metal stripping potential to a cleaning potential between about 1.2 V and about 1.6 V, and holding the cleaning potential for about 2 seconds to about 10 seconds;a pre-plating step including pulsing from the cleaning potential to a pre-plating potential between about −0.2 V and about −0.5 V, and holding the pre-plating potential for about 2 seconds to about 10 seconds;an equilibration step including pulsing from the pre-plating potential to the open circuit potential, and holding the open circuit potential for about 10 seconds to about 60 seconds; anda metal deposition step including scanning from the open circuit potential of the equilibration step to an additive desorption potential, and holding the desorption potential for about 1 second to about 30 seconds, scanning to an additive adsorption potential and holding the adsorption potential for about 5 seconds to about 30 seconds, and scanning from the additive adsorption potential to the open circuit potential;repeating the series of measurement steps until a steady state is reached;determining a profile of a deposition current resulting from the metal deposition potential as a function of time, and integrating the deposition current over the additive desorption potential to determine the concentration of the additive to be measured; andaveraging the deposition currents from the series of measurement steps when steady state has been reached to determine the concentration of the additive to be measured.28. A cyclic voltammetric method for measuring the concentration of additives in a plating solution, comprising:cycling the potential of a working electrode through a series of measurement steps, comprising a metal stripping step, a cleaning step, a pre-plating step, an equilibration step, and a metal deposition step; anddetermining a profile of a deposition current resulting from the metal deposition potential as a function of time and integrating the deposition current to determine the concentration of the additive to be measured.29. The method of claim 28, wherein the metal stripping step further comprises pulsing from an open circuit potential to a metal stripping potential between about 0.2 V and about 0.8 V, and holding the metal stripping potential until a corresponding current is about 0 mA/cm.30. The method of claim 29, wherein the metal stripping step further comprises holding the metal stripping potential for about 2 seconds to about 10 seconds.31. The method of claim 29, wherein the metal stripping potential is between about 0.4 V and about 0.6 V.32. The method of claim 28, wherein the cleaning step further comprises pulsing from a metal stripping potential to a cleaning potential between about 1.2 V and about 1.6 V and holding the cleaning potential for about 2 seconds to about 10 seconds.33. The method of claim 28, wherein the pre-plating step further comprises pulsing from a cleaning potential to a pre-plating potential between about −0.2 V and about −0.5 V and holding the pre-plating potential for about 2 seconds to about 10 seconds.34. The method of claim 28, wherein the equilibration step includes pulsing from a pre-plating potential to an open circuit potential, and holding the open circuit potential for about 10 seconds to about 60 seconds.35. The method of claim 28, wherein the equilibration step includes pulsing from a pre-plating potential to a stable open circuit potential, and holding the open circuit potential for about 5 seconds to about 10 seconds.36. The method of claim 28, wherein the metal deposition step includes scanning from an open circuit potential of the equilibration step to an additive sensitive potential, holding the additive sensitive potential for about 1 second to about 30 seconds, and scanning back to the open circuit potential.37. The method of claim 28, wherein the metal deposition step comprises scanning to an additive desorption potential, and holding the desorption potential until substantially all of the additive desorbs from the working electrode surface, scanning to an additive adsorption potential, and holding the adsorption potential for about 5 seconds to about 30 seconds, and scanning from the additive adsorption potential to the open circuit potential.38. The method of claim 37, wherein the additive desorption potential is held constant for about 1 second to about 30 seconds.39. The method of claim 28, wherein the series of measurement steps is repeated until a steady state is reached.40. The method of claim 39, wherein profiles from the deposition charges when steady state has been reached are averaged to determine the concentration of the additive to be measured.41. The method of claim 28, wherein the series of measurement steps is repeated from about 1 to about 5 times.42. A cyclic voltammetric method for measuring the concentration of additives in a plating solution, comprising:cycling the potential of a working electrode through a series of measurement steps, comprising a metal stripping step, a cleaning step, a pre-plating step, an equilibration step, and a metal deposition step, wherein the metal stripping step further comprises pulsing from an open circuit potential to a metal stripping potential between about 0.4 V and about 0.6 V, and holding the metal stripping potential until a corresponding current is about 0 mA/cm; anddetermining a profile of a deposition current resulting from the metal deposition potential as a function of time and integrating the deposition current to determine the concentration of the additive to be measured.43. A cyclic voltammetric method for measuring the concentration of additives in a plating solution, comprising:cycling the potential of a working electrode through a series of measurement steps, comprising a metal stripping step, a cleaning step, a pre-plating step, an equilibration step, and a metal deposition step, wherein the metal deposition step includes scanning from an open circuit potential of the equilibration step to an additive sensitive potential, holding the additive sensitive potential for about 1 second to about 30 seconds, and scanning back to the open circuit potential; anddetermining a profile of a deposition current resulting from the metal deposition potential as a function of time and integrating the deposition current to determine the concentration of the additive to be measured.44. A cyclic voltammetric method for measuring the concentration of additives in a plating solution, comprising:cycling the potential of a working electrode through a series of measurement steps, comprising a metal stripping step, a cleaning step, a pre-plating step, an equilibration step, and a metal deposition step, wherein the metal deposition step comprises scanning to an additive desorption potential, and holding the desorption potential until substantially all of the additive desorbs from the working electrode surface, scanning to an additive adsorption potential, and holding the adsorption potential for about 5 seconds to about 30 seconds, and scanning from the additive adsorption potential to the open circuit potential; anddetermining a profile of a deposition current resulting from the metal deposition potential as a function of time and integrating the deposition current to determine the concentration of the additive to be measured.45. The method of claim 44, wherein the additive desorption potential is held constant for about 1 second to about 30 seconds.46. A cyclic voltammetric method for measuring the concentration of additives in a plating solution, comprising:cycling the potential of a working electrode through a series of measurement steps, comprising a metal stripping step, a cleaning step, a pre-plating step, an equilibration step, and a metal deposition step; anddetermining a profile of a deposition current resulting from the metal deposition potential as a function of time and integrating the deposition current to determine the concentration of the additive to be measured, wherein the series of measurement steps is repeated until a steady state is reached and profiles from the deposition charges are averaged when the steady state has been reached.
BACKGROUND OF THE INVENTION
1. Field of the Invention
Embodiments of the invention generally relate to analysis of plating solutions, and more particularly, to the analysis of additives in plating solutions.
2. Description of the Related Art
Metallization of sub-quarter micron sized features is a foundational technology for present and future generations of integrated circuit manufacturing processes. More particularly, in devices such as ultra large scale integration-type devices, i.e., devices having integrated circuits with more than a million logic gates, the multilevel interconnects that lie at the heart of these devices are generally formed by filling high aspect ratio interconnect features with a conductive material, such as copper or aluminum, for example. Conventionally, deposition techniques such as chemical vapor deposition (CVD) and physical vapor deposition (PVD) have been used to fill interconnect features. However, as interconnect sizes decrease and aspect ratios increase, efficient void-free interconnect feature fill via conventional deposition techniques becomes increasingly difficult. As a result thereof, plating techniques, such as electrochemical plating (ECP) and electroless plating, for example, have emerged as viable processes for filling sub-quarter micron sized high aspect ratio interconnect features in integrated circuit manufacturing processes.
In an ECP process, for example, sub-quarter micron sized high aspect ratio features formed into the surface of a substrate may be efficiently filled with a conductive material, such as copper, for example. ECP plating processes are generally two stage processes, wherein a seed layer is first formed over the surface and features of the substrate, and then the surface and features of the substrate are exposed to a plating solution, while an electrical bias is simultaneously applied between the substrate and an anode positioned within the plating solution. The plating solution is generally rich in ions to be plated onto the surface of the substrate, and therefore, the application of the electrical bias causes these ions to be urged out of the plating solution and to be plated onto the seed layer. Furthermore, the plating solution generally contains organic additives, such as, for example, levelers, suppressors, and accelerators that are configured to increase the efficiency and controllability of the plating process. These additives are generally maintained within narrow tolerances, so that the repeatability and controllability of the plating operation may be maintained and repeated.
Monitoring and/or determining the composition of a plating solution during an ECP process is problematic, as the depletion of certain additives is not necessarily constant over a period of time, nor is it always possible to correlate the plating solution composition with the plating solution use. As such, it is difficult to determine the concentration of additives in a plating solution with any degree of accuracy over time, as the level of additives may either decrease or increase during plating, and therefore, the additive concentrations may eventually exceed or fall below the tolerance range for optimal and controllable plating. Conventional ECP systems generally utilize a cyclic voltammetric stripping (CVS) or a cyclic pulse voltammetric stripping (CPVS) process to determine the organic additive concentrations in the plating solution. In a CVS process, for example, the potential of a working electrode is swept through a voltammetric cycle that includes both a metal plating range and a metal stripping range. The potential of the working electrode is swept through at least two baths of non-plating quality, and an additional bath where the quality or concentration of organic additives therein is unknown. In this process, an integrated or peak current used during the metal stripping range may be correlated with the quality, i.e., concentration of additives, of the non-plating bath. As such, an integrated or peak current may be compared to the correlation of the non-plating bath, and the quality of the unknown plating bath determined therefrom. The amount of metal deposited during the metal plating cycle and then redissolved into the plating bath during the metal stripping cycle generally correlates to the concentration of particular organics, generally brighteners or accelerators, in the plating solution. Therefore, CVS methods generally observe the current density of the copper ions reduced on an electrode at a predetermined potential. Inasmuch as accelerators and brighteners increase the current density, the quantity of both may be determined from the observation.
However, one challenge associated with utilizing conventional CVS methods for determining the concentration of organics in a plating solution is that by-products, such as organic contaminants generated in plating processes, may interfere with the analysis process. More particularly, by-products essentially compete with additives for adsorption sites in certain potential ranges, and therefore, if the analysis scanning range includes the by-product adsorption range, the analysis of the unknown additive concentration may be affected by the adsorption of the by-products. Furthermore, the effect of the by-products on the additive analysis is amplified at higher working electrode rotation rates because the by-products and additives diffuse at a faster rate. Another challenge associated with conventional CVS methods is that a wide potential scanning range generally is used to ensure analysis reproducibility, thereby resulting in a relatively long time between analysis and correction.
CPVS processes attempt to overcome the challenges of conventional CVS processes by sequentially pulsing the working electrode between metal plating, stripping, cleaning, and equilibration steps to maintain the working electrode surface in a relatively clean and reproducible condition. CPVS generally avoids the by-product adsorption potential range by pulsing to the known additive adsorption potential range, i.e., by moving directly from an open circuit potential to a potential within the additive adsorption range without scanning through the by-product adsorption range. The steady-state charge density corresponding to the stripping step is then proportional to the additive concentration.
However, CPVS is not without challenges. For example, CPVS generally does not provide control over the rate of the forward reaction for metal deposition. Therefore, separation of interference is difficult. Due to the strong interaction among multiple additives competing for working electrode surface adsorption sites, the analysis of any one single additive may suffer from the interference of the other additives. As such, there is a need for a method for measuring additives in a plating solution, wherein the method is not susceptible to the inaccuracies of conventional analysis processes.
SUMMARY OF THE INVENTION
Embodiments of the invention generally relate to a cyclic voltammetric method for measuring the concentration of additives in a plating solution. The method generally includes providing the plating solution having an unknown concentration of an additive to be measured therein, and cycling the potential of an inert working electrode in contact with the plating solution through a series of measurement steps. The series of measurement steps generally includes a metal stripping step, including pulsing from an open circuit potential to a metal stripping potential between about 0.2 V and about 0.8 V, and holding the metal stripping potential until a corresponding current is about 0 mA/cm. The series of measurement steps further includes a cleaning step including pulsing from the metal stripping potential to a cleaning potential between about 1.2 V and about 1.6 V, and holding the cleaning potential for about 2 seconds to about 10 seconds. The series of measurement steps then includes a pre-plating step including pulsing from the cleaning potential to a pre-plating potential between about −0.2 V and about −0.5 V, and holding the pre-plating potential for about 2 seconds to about 10 seconds. The series of measurement steps may additionally include an equilibration step including pulsing from the pre-plating potential to the open circuit potential and holding the open circuit potential for a predetermined period, and a metal deposition step including scanning from the open circuit potential of the equilibration step to an additive sensitive potential, holding the additive sensitive potential for about 1 second to about 30 seconds, and scanning back to the open circuit potential. The method may further include determining a profile of a deposition current resulting from the metal deposition potential as a function of time and integrating the deposition current to determine the concentration of the additive to be measured.
Embodiments of the invention further provide a method for measuring the concentration of additives in a plating solution. The method generally includes cycling the potential of an inert working electrode through a series of measurement steps. The series of measurement steps generally includes a metal stripping step including pulsing from an open circuit potential to a metal stripping potential sufficient to remove substantially all metal on the working electrode, and holding the metal stripping potential until a corresponding current nears 0 mA/cm. The series of measurement steps then includes a cleaning step including pulsing from the metal stripping potential to a cleaning potential and holding the cleaning potential for about 2 seconds to about 10 seconds. The series of measurement steps further includes a pre-plating step including pulsing from the cleaning potential to a pre-plating potential sufficient to plate a layer of metal on the working electrode, and holding the pre-plating potential for about 2 seconds to about 10 seconds, and an equilibration step including pulsing from the pre-plating potential to the open circuit potential, and holding the open circuit potential for a predetermined period. The series of measurement steps additionally includes a metal deposition step including scanning from the open circuit potential of the equilibration step to an additive sensitive potential, holding the additive sensitive potential for about 1 second to about 30 seconds, and scanning back to the open circuit potential. The method further includes determining a profile of a deposition current resulting from the metal deposition potential as a function of time and integrating the deposition current to determine the concentration of the additive to be measured.
Embodiments of the invention further provide a cyclic voltammetric method for measuring the concentration of additives in a plating solution. The method generally includes cycling the potential of an inert working electrode through a series of measurement steps. The series of measurement steps include a metal stripping step which includes pulsing from an open circuit potential to a metal stripping potential between about 0.4 V and about 0.6 V, and holding the metal stripping potential for about 2 seconds to about 10 seconds, and a cleaning step including pulsing from the metal stripping potential to a cleaning potential between about 1.2 V and about 1.6 V, and holding the cleaning potential for about 2 seconds to about 10 seconds. The series of measurement steps further includes a pre-plating step including pulsing from the cleaning potential to a pre-plating potential between about −0.2 V and about −0.5 V, and holding the pre-plating potential for about 2 seconds to about 10 seconds, and an equilibration step including pulsing from the pre-plating potential to the open circuit potential, and holding the open circuit potential for about 10 seconds to about 60 seconds. The series of measurement steps additionally includes a metal deposition step including scanning from the open circuit potential of the equilibration step to an additive sensitive potential, holding the additive sensitive potential for about 1 second to about 30 seconds, and scanning back to the open circuit potential. The method further includes repeating the series of measurement steps until steady state is reached, determining a profile of a deposition current resulting from the metal deposition potential as a function of time and integrating the deposition current to determine the concentration of the additive to be measured, and averaging the deposition currents from the series of measurement steps when steady state has been reached to determine the concentration of the additive to be measured.
Embodiments of the invention further provide a cyclic voltammetric method for measuring the concentration of additives in a plating solution. The method generally includes providing the plating solution having an unknown concentration of an additive to be measured therein and cycling the potential of an inert working electrode through a series of measurement steps. The series of measurement steps includes a metal stripping step including pulsing from an open circuit potential to a metal stripping potential between about 0.4 V and about 0.6 V, and holding the metal stripping potential for about 2 seconds to about 10 seconds, and a cleaning step including pulsing from the metal stripping potential to a cleaning potential between about 1.2 V and about 1.6 V, and holding the cleaning potential for about 2 seconds to about 10 seconds. The series of measurement steps further includes a pre-plating step including pulsing from the cleaning potential to a pre-plating potential between about −0.2 V and about −0.5 V and holding the pre-plating potential for about 2 seconds to about 10 seconds, and an equilibration step including pulsing from the pre-plating potential to the open circuit potential, and holding the open circuit potential for about 10 seconds to about 60 seconds. The series of measurement steps additionally includes a metal deposition step including scanning from the open circuit potential of the equilibration step to an additive desorption potential and holding the desorption potential for about 1 second to about 30 seconds, scanning to an additive adsorption potential and holding the adsorption potential for about 5 seconds to about 30 seconds, and scanning from the additive adsorption potential to the open circuit potential. The method further includes repeating the series of measurement steps until steady state is reached, determining a profile of a deposition current resulting from the metal deposition potential as a function of time and integrating the deposition current over the additive desorption potential to determine the concentration of the additive to be measured, and averaging the deposition currents from the series of measurement steps when steady state has been reached to determine the concentration of the additive to be measured.
Embodiments of the invention also provide a cyclic voltammetric method for measuring the concentration of additives in a plating solution. The method generally includes the step of cycling the potential of a working electrode through a series of measurement steps, comprising a metal stripping step, a cleaning step, a pre-plating step, an equilibration step, and a metal deposition step. The method also may include the step of determining a profile of a deposition current resulting from the metal deposition potential as a function of time and integrating the deposition current to determine the concentration of the additive to be measured.
BRIEF DESCRIPTION OF THE DRAWINGS
So that the manner in which the above recited features of the present invention can be understood in detail, a more particular description of the invention, briefly summarized above, may be had by reference to the embodiments thereof, which are illustrated in the appended drawings. It is to be noted, however, that the appended drawings illustrate only typical embodiments of this invention, and are therefore, not to be considered limiting of its scope, for the invention may admit to other equally effective embodiments.
FIG. 1
is an exemplary embodiment of a plating system of the invention.
FIG. 2
is a cross section of a plating solution analysis device.
FIG. 3
shows the output of an exemplary embodiment of the invention.
FIG. 4
shows the output of an alternative embodiment of the invention.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT
FIG. 1
illustrates an exemplary plating system
100
of the invention. The plating system
100
generally includes a plating cell
101
, which may be, for example, an ECP plating cell configured to electrochemically plate copper onto a semiconductor substrate. The plating cell
101
may be selectively in fluid communication with a plating solution tank
103
configured to maintain a large volume of plating solution, approximately 200 liters, for example. The plating solution tank
103
may be configured to supply a plating solution stored therein to the plating cell
101
via a plating solution supply conduit
106
and return solution to tank
103
via a return conduit
107
. The supply conduit
106
may be in fluid communication with a plating solution analysis device
105
configured to sample a portion of the plating solution flowing therethrough to determine the quantity of various components in the sampled portion of the plating solution. The plating system
100
may further include a chemical cabinet
102
having one or more chemical storage units
104
positioned therein or in fluid communication therewith. The chemical cabinet
102
, and in particular, chemical storage units
104
, may be selectively in fluid communication with the plating solution tank
103
via a chemical supply conduit
110
.
Additionally, the plating system
100
may include a system controller
122
, which may be a microprocessor-based controller, for example, configured to control the operation of the respective components of the plating system
100
. The system controller
122
may be in electrical communication with the components of the plating cell
101
via an electrical conduit
108
, with the components of the plating solution analysis device
105
via an electrical conduit
111
, and with the components of chemical cabinet
102
via an electrical conduit
109
. As such, the system controller
112
may receive inputs from the various components of plating system
100
and generate control signals that may be transmitted to the respective components of the plating system
100
for controlling the operation thereof. For example, the system controller
122
may be configured to control parameters such as the flow rate of plating solution into the plating cell
101
, the timing and quantity of chemicals added to the plating solution by the chemical cabinet
102
, and the operational characteristics of the plating cell
101
, along with other parameters generally associated with ECP systems and ECP solution analysis.
FIG. 2
illustrates a plating solution analysis device
105
useful in practicing the present invention. Three electrodes, a working electrode
202
, a counter electrode
204
, and a reference electrode
206
, are generally immersed in a cell
208
having plating solution to be measured therein. The counter electrode
204
provides an internal standard which mitigates the effects of other plating solution constituents and changes in the state of the working electrode
202
surface. The counter electrode
204
is generally selected and designed so as not to be easily polarized in the particular plating solution being evaluated. This is accomplished, in part, by placing the counter electrode
204
close to the working electrode
202
. The working electrode
202
is generally a metal disk, such as platinum, copper, nickel, chromium, zinc, tin, gold, silver, lead, cadmium, solder, glassy carbon, mercury, or stainless steel, for example. The working electrode
202
typically has a flat, polished surface, small diameter, and may be mounted flush with the end of a cylinder. A small diameter disk is generally preferred, since a larger diameter generally results in poor sensitivity due to non-uniform current density across the diameter. Other suitable working electrodes
202
include any electrode that provides a uniform current density and controlled agitation. The reference electrode
206
may, for example, be a saturated Calomel reference electrode (SCE), a silver electrode saturated with silver chloride, or a platinum electrode. To establish relative motion between the working electrode
202
and the plating solution, a motor
210
may be used to rotate the working electrode
202
. Without such motion, the plating solution generally becomes depleted at the surface of the working electrode
202
and the deposition rate obtained may not reflect the correct rate for the plating solution. Other means of obtaining relative motion can be used, such as a pump for moving the plating solution across the face of the working electrode
202
.
A computer
212
generally controls an electronic potentiostat
214
, which controls the energy input of the working electrode
202
relative to the reference electrode
206
. Using a suitable program, specific energy input sequences of the present invention may be applied to the working electrode
202
. The output of the device
105
can also be plotted on an X-Y recorder for each step. The following description of embodiments of the invention will be described by reference to the energy input as current and energy output as potential, and will be described by reference to standard acid/copper electroplating solutions. It is possible however to use the method to control other metal solutions such as nickel, chromium, zinc, tin, gold, silver, lead, cadmium, and solder, for example.
Embodiments of the invention generally employ copper plating solutions having copper sulfate at a concentration between about 5 g/L and about 100 g/L, an acid at a concentration between about 5 g/L and about 200 g/L, and halide ions, such as chloride, at a concentration between about 10 ppm and about 200 ppm, for example. The acid may include sulfuric acid, phosphoric acid, and/or derivatives thereof. In addition to copper sulfate, the plating solution may include other copper salts, such as copper fluoborate, copper gluconate, copper sulfamate, copper sulfonate, copper pyrophosphate, copper chloride, or copper cyanide, for example. However, embodiments of the invention are not limited to these parameters.
The electroplating solution may further include one or more additives. Additives, which may be, for example, levelers, inhibitors, suppressors, brighteners, accelerators, or other additives known in the art, are typically organic materials that adsorb onto the surface of the substrate being plated and have an affect on plating characteristics. Useful suppressors typically include polyethers, such as polyethylene, glycol, or other polymers, such as polypropylene oxides, which adsorb on the substrate surface, slowing down copper deposition in the adsorbed areas. Useful accelerators typically include sulfides or disulfides, such as bis(3-sulfopropyl)disulfide, which compete with suppressors for adsorption sites, accelerating copper deposition in adsorbed areas. Useful inhibitors typically include sodium benzoate and sodium sulfite, which inhibit the rate of copper deposition on the substrate. During plating, the additives are consumed at the substrate surface, but are being constantly replenished by the plating solution. However, differences in diffusion rates of the various additives result in different surface concentrations at the top and the bottom of the features, thereby setting up different plating rates in the features. Ideally, these plating rates should be higher at the bottom of the feature for bottom-up fill. Thus, an appropriate composition of additives in the plating solution is required to achieve a void-free fill of the features.
The additive concentrations in the plating solution generally should remain in the low ppm range, e.g., less than 5 ppm, to obtain acceptable deposits. For example, when the accelerator level is insufficient, the copper deposits are burnt and powdery. Excess accelerator induces brittleness and a nonuniform deposition on the substrate surface. Additive concentrations fluctuate as a result of oxidation at the anode, reduction and inclusion at the cathode and chemical reactions. Since the additive concentrations are continually fluctuating within the plating solution, it is necessary to minimize the time between chemical analysis and correction of the additive concentration within the plating solution.
FIG. 3
illustrates a voltage signal for an exemplary embodiment of the invention. Embodiments of the invention include cycling the working electrode
202
through a sequence of steps, including a stripping
300
, cleaning
302
, pre-plating
304
, equilibration
306
, and metal deposition step
308
. The steps prior to the metal deposition step
308
include several distinct pulses to provide increased additive sensitivity and reproducibility of the results. The metal stripping step
300
includes pulsing the potential between the working electrode
202
and the reference electrode
206
from an initial voltage, for example, from the open circuit potential, to a potential between about 0.2 V and about 0.8 V, i.e., the metal stripping potential, until the corresponding current is approximately 0 mA/cm, for example, about 2 seconds to about 10 seconds. As used herein, the term “pulse” refers to immediately applying a desired potential from a prior potential. Next, the potential is pulsed to about 1.2 V to about 1.6 V, i.e., the cleaning potential, for about 2 seconds to about 10 seconds to clean the working electrode
202
in the cleaning step
302
. A thin layer of metal is then plated onto the surface of the working electrode
202
in a pre-plating step
304
by pulsing to a potential between about −0.2 V and about −0.5 V, i.e., the pre-plating potential, for about 2 seconds to about 10 seconds. The potential is then pulsed back to the open circuit potential in an equilibration stage
306
for a predetermined time period, for example, about 10 seconds to about 60 seconds. The final step is a metal deposition step
308
. The deposition step
308
includes scanning to an additive sensitive potential
310
, i.e., a potential where the additive desorbs from the working electrode, holding the additive sensitive potential
312
for about 1 to about 30 seconds, and reversing the potential and scanning back
314
to the open circuit potential. As used herein, the term “scan” refers to linearly ramping to a desired potential from a prior potential. The additive sensitive potential may vary and is dependent on the additive to be measured.
As a result of linear scanning, the rate of metal deposition is sensitive to the presence and concentration of additives present in the plating solution. Therefore, the amount of electricity spent for metal deposition, Q
c
, changes depending on the composition of the plating solution. Selection of the proper scan rate, the deposition potential range, and the working electrode rotational speed help to make the Q
c
more sensitive to the additive to be analyzed by further reducing the effects of the other constituents in the plating solution. Varying the scan rate separates slow processes from fast process. In addition, the use of various rotational speeds allows for additive transport control. Embodiments of the invention contemplate repeating the above sequence until steady state is reached, i.e., until two sequential values agree within about 2%, for example, between 2 to 5 cycles. The average of the steady state data obtained from the last cycles is generally used to estimate the unknown additive concentration.
The additive concentration is then determined by integrating the current over the metal deposition time period
308
, resulting in a deposition charge, and comparing the deposition charge to deposition charges for known plating solutions. Conventional methods measure the additive concentration by integrating the current over the metal stripping time period
300
. By integrating the current over the metal deposition time period
308
, rather than the stripping step
300
, embodiments of the present invention reduce the noise produced by other constituents in the plating solution.
Embodiments of the invention further contemplate an equilibration stage
306
, wherein the potential of the working electrode
202
is pulsed to a stable open circuit potential for about 5 seconds to about 10 seconds. The stable open circuit potential is pre-determined by measuring the open circuit potential after about 60 seconds.
FIG. 4
illustrates the output of an alternative embodiment of the invention. Embodiments of the invention further contemplate a metal deposition step
308
including scanning to a potential where the additive desorbs from the working electrode
202
, i.e., the additive desorption potential
400
, and holding that potential
400
for about 1 second to about 30 seconds so that the additive completely desorbs from the working electrode
202
. The potential is then scanned back to a potential where the additive adsorbs onto the working electrode
202
surface, i.e., the additive adsorption potential
402
, and is held for about 5 seconds to about 30 seconds. The potential is then scanned back to the open circuit potential.
While the foregoing is directed to embodiments of the present invention, other and further embodiments of the invention may be devised without departing from the basic scope thereof, and the scope thereof is determined by the claims that follow.
标题 | 发布/更新时间 | 阅读量 |
---|---|---|
一种用于水体中重金属快速检测的分析方法 | 2020-05-13 | 89 |
石墨烯-石墨烯纳米带海绵的制备表征及性能测试的方法 | 2020-05-13 | 590 |
一种氮化铝底板与铜热沉复合体的制备方法 | 2020-05-08 | 474 |
一种血液样本类型识别检测系统 | 2020-05-14 | 665 |
基于核酸适配体的镉离子电化学传感方法 | 2020-05-11 | 807 |
一种Pt(IV)-5-CN-PADAT络合物/其修饰电极/电化学传感器和其应用 | 2020-05-12 | 483 |
一种基于碳纳米管聚多巴胺复合材料微生物燃料电池的方法 | 2020-05-14 | 770 |
一种发光细菌检测土壤重金属综合含量的方法及其应用 | 2020-05-11 | 578 |
具有可交联基团的平面型三苯胺衍生物及其合成方法 | 2020-05-12 | 745 |
一种杂多酸/还原氧化石墨烯/聚吡咯复合材料及其制备方法和应用 | 2020-05-11 | 412 |
高效检索全球专利专利汇是专利免费检索,专利查询,专利分析-国家发明专利查询检索分析平台,是提供专利分析,专利查询,专利检索等数据服务功能的知识产权数据服务商。
我们的产品包含105个国家的1.26亿组数据,免费查、免费专利分析。
专利汇分析报告产品可以对行业情报数据进行梳理分析,涉及维度包括行业专利基本状况分析、地域分析、技术分析、发明人分析、申请人分析、专利权人分析、失效分析、核心专利分析、法律分析、研发重点分析、企业专利处境分析、技术处境分析、专利寿命分析、企业定位分析、引证分析等超过60个分析角度,系统通过AI智能系统对图表进行解读,只需1分钟,一键生成行业专利分析报告。