LIQUID CRYSTAL COMPOSITION AND DISPLAY DEVICE THEREOF
专利汇可以提供LIQUID CRYSTAL COMPOSITION AND DISPLAY DEVICE THEREOF专利检索，专利查询，专利分析的服务。并且A liquid crystal composition and a liquid crystal display wherein the liquid crystal composition includes: a compound of general formula (I) including 1%-50% of the total weight of the liquid crystal composition; a compound of general formula (II) including 1%-60% of the total weight of the liquid crystal composition; a compound of general formula (III) including 1%-60% of the total weight of the liquid crystal composition; and a compound of general formula (IV) including 0-50% of the total weight of the liquid crystal composition—wherein the liquid crystal composition has a suitably wider nematic phase scope, a suitable optical anisotropy, a favorable low-temperature storage stability a faster response speed, can be used for outdoor work, has a good image display effect, and substantially free of streaking phenomenon.，下面是LIQUID CRYSTAL COMPOSITION AND DISPLAY DEVICE THEREOF专利的具体信息内容。
The present invention relates to a liquid crystal composition, and specifically relates to a liquid crystal composition having a higher response speed, a broader range of a nematic phase and a favourable low-temperature storage stability and the use thereof.
Liquid crystal material is a mixture of organic rod-shaped small molecular compounds which has both liquid fluidity and anisotropy of crystal in a certain temperature. Because of its optical anisotropy and dielectric anisotropy characteristics, liquid crystal material is widely used in the liquid crystal display elements of the devices of electronic calculators, car dashboard, televisions, computers and the like. Based on the LCD modes, liquid crystal compositions can be classified into the types of twisted nematic (TN), super twisted nematic (STN), thin film transistor (TFT), guest-host (GH), dynamic scattering (DS) and the like. The most common display element therein is based on the Schadt-Helfrich effect and has a twisted nematic structure.
Liquid crystal materials are required to have good chemical and heat stability, a suitable optical anisotropy, a broader range of a nematic phase as well as the good stabilities to electric field and electromagnetic radiation. In addition, the liquid crystal materials should have low viscosity and produce low threshold voltage and high contrast ratio in the liquid crystal cell. Since liquid crystal material is normally used as a mixture of various components, it is especially important that these components are miscible with each other. However, as the optimization of each performance parameter of the mixed liquid crystal material may result in inter-contradictory, inter-constraint and inter-influence results, it is very difficult to achieve a broader range of a nematic phase, suitable refractivity and dielectric anisotropy, as well as low-temperature storage stability at the same time. For example, the obvious defects of the liquid crystal compositions of EP0667555, EP0673986, DE19528106, DE19528107 and WO962851 are having a longer response time, lower resistivity and overhigh operating voltage. Further, poor low-temperature storage stability is also a defect of various existing liquid crystal materials.
Therefore, in the field of liquid crystal material, there is a need for novel liquid crystal compositions with improved performances. Particularly, for many types of application, liquid crystal compositions should have a suitably broader range of a nematic phase, a suitable refractivity and dielectric anisotropy, and a low-temperature storage stability.
One object of the present invention is to provide a liquid crystal composition having a higher response speed, a broader range of a nematic phase and a favourable low-temperature storage stability through optimizing the combinations of various liquid crystal compositions and the formulations thereof. The liquid crystal compositions will not show the defects in the existing materials or at least only show the above defects in a significantly lower degree.
In order to achieve the aforementioned object of the invention, the present invention provides a liquid crystal composition which comprises four compounds conforming with the following structural general formulas I, II, III and IV, wherein:
(1) 1%-50% by weight of the total amount of the liquid crystal composition of a compound of general formula (I)
(2) 1%-60% by weight of the total amount of the liquid crystal composition of a compound of general formula (II)
(3) 1%-60% by weight of the total amount of the liquid crystal composition of a compound of general formula (III)
and
(4) 0%-50% by weight of the total amount of the liquid crystal composition of a compound of general formula (IV)
in which:
R1, R2, R3, R4, R5 and R6 can be same or different, and are independently selected from a group consisting of H, halogen, C1-C7 alkyl, C1-C7 alkoxy, C2-C7 alkenyl and C2-C7 alkenoxy, in which one or more H of the C1-C7 alkyl, C1-C7 alkoxy, C2-C7 alkenyl and C2-C7 alkenoxy can be independently substituted by F;
Z1-Z5 can be same or different, and are independently selected from a group consisting of single bond, —CH═CH—, —C≡C—, —O—, —COO—, —COO—, —OCH2—, —C2H4—, —CH2O— and —CF2O—;
X1 is selected from a group consisting of halogen, C1-C7 alkyl, C1-C7 alkoxy and C2-C7 alkenoxy, in which one or more H of the C1-C7 alkyl, C1-C7 alkoxy and C2-C7 alkenoxy can be independently substituted by F;
L1-L6 can be same or different, and independently are H or F, in which, at lease two of the L1-L6 are F;
are independently selected from a group consisting of
in which, one or more H of the
can be independently substituted by F;
m, n and s independently are 0 or 1, and n and s are not simultaneously 0.
In the embodiments of the present invention, preferably, the compound of general formula (I) accounts for 3%-45% by weight of the total amount of the liquid crystal composition; the compound of general formula (II) accounts for 2%-50% by weight of the total amount of the liquid crystal composition; the compound of general formula (III) accounts for 3%-45% by weight of the total amount of the liquid crystal composition; and the compound of general formula (IV) accounts for 5%-40% by weight of the total amount of the liquid crystal composition.
In the embodiments of the present invention, preferably, the compound of general formula (I) is one or more compounds selected from a group consisting of the following compounds:
in which:
R1 is selected from a group consisting of C1-C5 alkyl, C1-C5 alkoxy, C2-C5 alkenyl and C2-C5 alkenoxy, in which one or more H of the C1-C5 alkyl, C1-C5 alkoxy, C2-C5 alkenyl and C2-C5 alkenoxy can be independently substituted by F;
X1 is selected from a group consisting of —F, —Cl, —CH2F, —CH2CH2F, —CH2CH2CH2F, —CH2CH2CH2CH2F, —OCF3, —OCH2F, —CH2OCH2F, —CH2CH2OCH2F, —CH═CH2 and —OCH═CF2.
In the embodiments of the present invention, preferably, the compound of general formula (II) is one or more compounds selected from a group consisting of the following compounds:
in which:
R2 is selected from a group consisting of C1-C5 alkyl, C1-C5 alkoxy, C2-C5 alkenyl and C2-C5 alkenoxy, in which one or more H of the C1-C5 alkyl, C1-C5 alkoxy, C2-C5 alkenyl and C2-C5 alkenoxy can be independently substituted by F.
In the embodiments of the present invention, preferably, the compound of general formula (III) is one or more compounds selected from a group consisting of the following compounds:
in which:
R3 is selected from a group consisting of C1-C5 alkyl, C1-C5 alkoxy, C2-C5 alkenyl and C2-C5 alkenoxy, in which one or more H of the C1-C5 alkyl, C1-C5 alkoxy, C2-C5 alkenyl and C2-C5 alkenoxy can be independently substituted by F.
In the embodiments of the present invention, preferably, the compound of general formula (IV) is one or more compounds selected from a group consisting of the following compounds:
in which:
R5 is selected from a group consisting of C1-C5 alkyl, C1-C5 alkoxy, C2-C5 alkenyl and C2-C5 alkenoxy, in which one or more H of the C1-C5 alkyl, C1-C5 alkoxy, C2-C5 alkenyl and C2-C5 alkenoxy can be independently substituted by F.
More preferably, the compound of general formula (I) is one or more compounds selected from a group consisting of the following compounds:
More preferably, the compound of general formula (II) is one or more compounds selected from a group consisting of the following compounds:
More preferably, the compound of general formula (III) is one or more compounds selected from a group consisting of the following compounds:
More preferably, the compound of general formula (IV) is one or more compounds selected from a group consisting of the following compounds:
In another aspect of the present invention, it provides a use of the liquid crystal composition of the present invention in manufacturing electrooptic device.
In yet another aspect of the present invention, it provides an electrooptic liquid crystal display comprising the liquid crystal composition of the present invention.
A liquid crystal medium comprising the aforementioned liquid crystal compositions with a broader range of nematic phase, a suitable optical anisotropy, a favourable low-temperature storage stability and a faster response time was established by the inventors through doing the combined experiments for the above compounds and comparing with the Comparison Examples.
As stated above, the liquid crystal compositions of the present invention can be used for outdoor work. The image display effect thereof is good, and there is no smearing phenomenon. Moreover, the liquid crystal compositions of the present invention have a favourable low-temperature storage stability and a higher response speed.
Unless specifically indicated, in the present invention, all ratios are weight ratios; all temperatures are degree centigrade; and the test on the data of the response time uses a cell gap of 7 nm.
The present invention will be illustrated by combining the detailed embodiments below. It should be noted that, the following examples are exemplary embodiments of the present invention, which are only used to illustrate the present invention, not to limit it. Other combinations and various modifications within the conception of the present invention are possible without departing from the subject matter and scope of the present invention.
The liquid crystal displays employed in the following embodiments are all TN-TFT liquid crystal display apparatus which is comprised of elements, such as polarizers (polaroids), electrode substrates, etc., and the cell gap thereof d=7 nm. This display apparatus is in normally white (NW) mode, i.e., white pixel color is observed if there is no voltage difference applied between the row electrode and the column electrode. The axes of the upper and lower polaroids on the substrates are at a 90-degree angle. The optical liquid crystal material is filled full of the space between the two substrates.
For the convenience of the expression, the unit structures of the liquid crystal compounds in the following Examples are represented by the codes listed in Table 1:
Take the following structural formula as an example:
Represented by the codes listed in Table 1, this structural formula can be expressed as 3PTGQP3.
Another example:
it can be expressed as nCPTPm, in which, the n in the code represents the number of the carbon atoms of the alkyl group on the left, for example, n is “3” means the alkyl is —C3H7; the C in the code represents a cyclohexyl; the P in the code represents phenylene; the T in the code represents alkynyl; the m in the code represents the number of the carbon atoms of the alkyl group on the right, for example, m is “1” means the right alkyl is —CH3.
The abbreviated codes of the test items in the following Examples are respectively represented as:
Cp ( ) clearing point (nematic-isotropy phase transition temperature)
Δn optical anisotropy (589 nm, 20° C.)
γ1 torque viscosity (mPa*s, below 20° C.)
K11 elastic constant (“splay”, pN below 20° C.)
K33 elastic constant (“bend”, pN below 20° C.)
t−30° C. storage lifetime at low-temperature (below −30° C.)
V90 saturation voltage=characteristic voltage at 90% relative contrast (NW mode)
V10 threshold voltage=characteristic voltage at 10% relative contrast (NW mode)
Test conditions of V10: C/1 KHZ, JTSB7.0.
The ingredients used in the following Examples are all synthesized by the inventors of the present application according to the methods known in the art. These synthetic techniques are routine, and the test results show that the liquid crystal compounds thus prepared meet the criteria for the electronic compounds.
Several liquid crystal compositions are prepared according to the formulations of the liquid crystal compositions specified in the following Examples. The preparation of the liquid crystal compositions is proceeded according to the conventional methods in the art, and as an example, the compositions are prepared by mixing the specified formulation via the processing modes, such as heating, ultrasonic processing, suspending processing and so on.
The liquid crystal composition specified in the following Examples are prepared and studied. The formulas of the liquid crystal compositions and their test results for the performance are shown below.
Table 2 and Table 5 show the formulations of the liquid crystal compositions of the Comparison Examples. The test results obtained from the liquid crystal display devices filled with the liquid crystal compositions of the Comparison Examples in the space between the two substrates of the liquid crystal display devices are also listed so that the performances of the liquid crystal composition of the present invention can be compared with those of the Comparison Examples clearly.
The liquid crystal composition of the Comparison Example is prepared according to the formulation listed in Table 2, and is tested by filling the same between two substrates of a liquid crystal display device. The performance data are shown in the Table below:
The liquid crystal composition of the invention is prepared according to the formulation listed in Table 3, and is tested by filling the same between two substrates of a liquid crystal display device. The performance data are shown in the Table below:
As compared with the Comparison Example, this liquid crystal composition has a suitable dielectric anisotropy and refractivity anisotropy, a high clearing point, a low threshold voltage and a large elastic constant with the advantages of a preferable display contrast, a high response speed and a lower power consumption for a liquid crystal composition, which is adapted for use in low-temperature environment.
The liquid crystal composition of the invention is prepared according to the formulation listed in Table 4, and is tested by filling the same between two substrates of a liquid crystal display device. The performance test data are shown in the Table below:
As compared with the Comparison Example, this liquid crystal composition has a suitable dielectric anisotropy and refractivity anisotropy, a high clearing point, a low threshold voltage and rotary viscosity, and a high elastic constant with the advantages of a preferable display contrast and a high response speed for a liquid crystal composition, which is applicable to outdoor equipments and is adapted for use in low-temperature environment.
The liquid crystal composition of the Comparison Example is prepared according to the formulation listed in Table 5 and is tested by filling the same between two substrates of a liquid crystal display device. The performance test data is shown in the Table below:
The liquid crystal composition of the invention is prepared according to the formulation listed in Table 6, and is tested by filling the same between two substrates of a liquid crystal display device. The performance test data are shown in the Table below:
As compared with the Comparison Examples, this liquid crystal composition has a suitable refractivity anisotropy, a higher clearing point, a low rotary viscosity and threshold voltage with the advantages of a very high response speed and superior power saving performance for a liquid crystal composition, which is adapted for use in low-temperature environment.
The liquid crystal composition of the invention is prepared according to the formulation listed in Table 7, and is tested by filling the same between two substrates of a liquid crystal display device. The performance test data are shown in the Table below:
As compared with the Comparison Examples, this liquid crystal composition has a suitable refractivity anisotropy and a lower threshold voltage with the advantages of a higher clearing point and a higher response speed for a liquid crystal composition, which is adapted for use in low-temperature environment.
The liquid crystal composition of the invention is prepared according to the formulation listed in Table 8, and is tested by filling the same between two substrates of a liquid crystal display device. The performance test data are shown in the Table below:
As compared with the comparison examples, this liquid crystal composition has a suitable refractivity anisotropy and a lower threshold voltage with the advantages of a high clearing point and a higher response speed for a liquid crystal composition, which is adapted for use in low-temperature environment.
The liquid crystal composition of the invention is prepared according to the formulation listed in Table 9, and is tested by filling the same between two substrates of a liquid crystal display device. The performance test data are shown in the Table below:
As compared with the Comparison Examples, this liquid crystal composition has a suitable refractivity anisotropy and a lower threshold voltage with the advantages of a higher clearing point and a higher response speed for a liquid crystal composition, which is being adapted for use in low-temperature environment.
| 标题 | 发布/更新时间 | 阅读量 |
|---|---|---|
| 一种基于各向异性过滤技术的异形曲面加筋拓扑优化方法 | 2020-05-08 | 843 |
| 一种充气薄膜可展抛物面天线及其获取方法 | 2020-05-08 | 383 |
| 微结构释放的方法及深硅刻蚀微结构 | 2020-05-11 | 623 |
| 一种制备超细晶铝及铝合金的复合大塑性变形方法 | 2020-05-08 | 33 |
| 交叉点存储器及其制造方法 | 2020-05-11 | 693 |
| 高性能PA66复合材料及其产品 | 2020-05-08 | 848 |
| 一种MEMS器件 | 2020-05-08 | 459 |
| 能有效降低激光增材制造钛合金各向异性的热处理方法 | 2020-05-08 | 427 |
| 掩膜板张网力的仿真预测方法及系统、掩膜板张网设备 | 2020-05-08 | 496 |
| 在不同磁阻随机存取存储器阵列中具有不同磁性隧道结的半导体管芯 | 2020-05-11 | 129 |
高效检索全球专利专利汇是专利免费检索,专利查询,专利分析-国家发明专利查询检索分析平台，是提供专利分析，专利查询，专利检索等数据服务功能的知识产权数据服务商。
我们的产品包含105个国家的1.26亿组数据，免费查、免费专利分析。
专利汇分析报告产品可以对行业情报数据进行梳理分析，涉及维度包括行业专利基本状况分析、地域分析、技术分析、发明人分析、申请人分析、专利权人分析、失效分析、核心专利分析、法律分析、研发重点分析、企业专利处境分析、技术处境分析、专利寿命分析、企业定位分析、引证分析等超过60个分析角度，系统通过AI智能系统对图表进行解读，只需1分钟，一键生成行业专利分析报告。
-
2 重合复合内饰零件