Process and composition for constructing hydraulically bonded road foundations or semirigid roadway structures
专利汇可以提供Process and composition for constructing hydraulically bonded road foundations or semirigid roadway structures专利检索，专利查询，专利分析的服务。并且According to the invention when building hydraulically bonded road foundations or semirigid roadway structures with known operations or when producing the material of road foundations, in addition to the usually applied hydraulic binding material, and to the usual additives, 50-150 kg/m³ of granular plastic material of 1-15 mm, preferably of 5-10 mm, particle size and of a specific surface of 6.0-0.2 kg/m² is added to the material of the road foundation.
The process can be performed by preliminary blending of the components or by admixing the grained plastic material to the existing soil or to the mineral material transported there and laid out on the site of the road building.，下面是Process and composition for constructing hydraulically bonded road foundations or semirigid roadway structures专利的具体信息内容。
The object of the invention is process and composition for constructing hydraulically bonded road foundations or semirigid roadway structures. The composition according to the invention contains grained (granulated) plastic material.
Because of a high increase in the price of bitumens, the upper bituminous layers (asphalt toppings) of roadway structures have become ever thinner in the last decade. There have been inevitably developed the so called semirigid roadway structures having hydraulically bonded lower and upper base layers both of relatively great thickness, on which layers an asphalt topping of maximum 10 cm total thickness is built. The mainly transverse contraction fissures ever arising in the hydraulically bonded base layers due to the contractions and expansions caused by the temperature differences, exert a stress on the asphalt topping resulting in it cracking through sooner or later. In the practice of many countries the cracking through of the asphalt toppings built on hydraulically bonded foundations is unwillingly acknowledged so that the early closing of the cracks is considered as an inevitable maintenance activity. Namely for lack of this there is not ensured the water-tightness of the roadway structure, leading to the decrease in the load-bearing capacity of the road, by which its lifetime can be much more reduced than by the effects of the vehicles.
The specific behaviour of the semirigid roadway structures and the technical problems caused by this are outlined by innumerable technical papers and publications. Nowadays on this theme there are regularly organized symposiums (e.g. in Lisbon, June 1985; in London, October 1986; special section of the Roadway World Congress in Brussels, 1987). The technical and economic advantages and disadvantages of building semirigid roadway structures are comprehensively outlined by three technical papers or publications as follows:
CAMOMILLA, MALGARINI: Cement mixed in highway Pavements. Dynamic real moduli in the different types on the "Autostrade" network. (Autostrade SPA, October, 1984).
GRÜFELFELDE: Erfahrungen mit vollstabilisierten Oberbau im Kanton Zürich. (Strasse und Verkehr, Januar, 1982).
Scellement des fissures. Recommandation sur les chaussées semi-rigides. Annexe XIII. E.C.E. TEM. 1985.
Preventing the cracking through of the thinner asphalt pavement on semirigid roadway structures is a technically sophisticated task which is, in our knowledge, not unambiguously solved in Europe up to now.
The technical solutions preventing the danger of cracking through have basically two trends:
- Between the base course and the asphalt pavement so called Stress Absorbing Membranes are set. The modificated bitumens with high elastomer content are suitable for forming this (membrane-like) layer which layer can be built in small thickness. This method has been used only recently and, according to the references of the technical literature is proving to be an effective technique. Its general use is made questionable by to the high cost effect of applying the modified bitumen, since in that way the advantage of building the semirigid roadway structures with lower cost is lost.
- The French firm COLAS has attempted to build a stress absorbing intermediate layer for a long time. In order to take the thermic-breathing movement of the hydraulically bonded base layer a 8 - 15 cm (!) thick bitumen-emulsive grained material, emulsive cold asphalt, is built between the base and the asphalt pavement. (LANGUMIER: Fini le temps des fissures. Revue Général des Routes et des Aérodromes, No. 617, 1985). Based on the experiences of the firm COLAS this method is also a promising one. However, the cost effects of building an intermediate layer of considerable thickness and the possible risk that in case of more significant traffic loadings, due to the lower stability of the emulsive intermediate layers detrimental deformations can arise in the asphalt surfacing that are disadvantageous.
The most obvious and economical solution trends are aimed at preventing the formation of wider fissures in the hydraulically bonded base course from the beginning. For that reason the continuity of the base is disrupted during the construction thus inhibiting the formation of transverse fissures of considerable width in greater distances, but promoting the formation of such fissures at short intervals and with small width. Such hair-cracked asphalt surfacing coworking with the hydraulic base already does not have such a deformability in the winter weather that could cause its cracking through or if after all the cracking through is caused it is formed only in a reduced degree. Several variations of the technique aiming at this are known from the practice of some greater foreign road building companies as follows:
- When building the hydraulic base so called blind gaps are formed at short intervals (of 3-5 m).
- The whole thickness of the hydraulic base course is formed by constructing several thinner layers.
- When building at laying, corrugated sheets made from plastic material are laid in a plane corresponding to the thicknesses 1/3 or 1/2.
- When mixing the material of the hydraulically bonded base course a bonding inhibitor agent is added, then the layer laid is rolled for a long time by very heavy paving rollers in order to "break" the material and to obtain a great number of haircracks.
The success of the above techniques can be estimated with difficulty. However, it is thought-provoking that, in our knowledge, there are no foreign technical prescriptions of state validity which would make obligatory the application of anyone of the techniques described above.
In order to avoid the formation of reflection cracks different methods have been developed as can also be seen from the technical literature sources mentioned already above:
- the limits of the maximum strength of the layer have been determined,
- the layer was broken by paving roller already during bonding,
- the asphalt was not stuck to the base course,
- only diluted bitumen was used, to reach the parameters required,
- so called stress absorbing membrane was built in as intermediate layer with high cost,
- the material continuity was disrupted by setting corrugated sheets from plastic material, etc.
The time of the appearance of the cracks was delayed by these methods, however, the later occurring cracks indicate that the problem is not solved yet.
The object of the invention is to change the internal structure of the hydraulically bonded road foundations in such away that the damaging effect of the continually working stresses of the hydraulic road foundations on the coworking asphalt surfacing should be prevented without reducing the load bearing capacity of the whole roadway structure.
We have realized that by adding suitable grained (granular) plastic material as additive into the hydraulically bonded road foundations, the plastic material particles weaken and distribute the arising tensile strength while the compressive strength of the road foundation remains practically unchanged. Due to the knocking against one another and deviation of the arising stresses in the hydraulically bonded base course prepared using grained plastic material additive the material functions like the traditional metal foundation and the asphalt does not crack through above it. (The panel-like cracking of concrete is followed by the cracking through of the asphalt.)
According to the invention, in compliance with those stated above, for preparing hydraulically bonded road foundations grained plastic material additive is used, wherein the plastic material particles are positioned in the road foundation as solid elements. Using this technique it is more advantageous to apply plastic material with smaller specific surface, i.e. larger grains within the range of 0,2-6,0 m²/kg of the specific surface. The cement mortar does not adhere to the grains of the plastic material having a specific surface of 0.2 - 6.0 m²/kg and is not bonded with them, thus due to the loading affecting on the structure and to the effects of temperature there is produced a network of haircracked system conforming to the position of the grains of plastic material. This form of fissuration comes into existence due to the arising stresses colliding with one another and changing their direction. Due to the haircracks a flexible roadway structure layer, similar to the metal foundation, is formed by the road foundation completed under the asphalt layer set on it, thus in this way the reflection breaking of the asphalt does not occur following the breaking of the traditional concrete foundations.
According to the invention the following process is realized: grained plastic material or grained plastic material waste is mixed in the required amount to the binding materials of the hydraulically bonded road foundations, so to the cement and/or basic fly ash or lime + fly ash binding materials and to the generally used additives, e.g. to sand-gravel, crushed gravel and/or to industrial waste products (e.g. fly ash, blast furnace cinder) and this composition blended with adequate volume of water is used for building the road foundation. The quality of the hydraulic binding material, the proportion of the water to the binding material, and the quality and quantity of the additives used if desired is chosen according to the usual practice of the road building. This road foundation is set on a surface with adequate load bearing capacity, then an asphalt surfacing is built on it according to the practice usual in the road building. Thus in the way according to the invention there can be built e.g. roads, footways, playing fields, reservoirs, etc.
Alternatively, the plastic material particles are mixed to the soil of the 20 cm top part of the earthwork or to the mineral material carried in the earthwork and stretched there in situ, i.e. the plastic material particles are brought into contact with the other components only on the site of road foundation building. (This technique is, according to the road building technology, the so called in situ stabilization method.)
For the purpose of road building an amount of the plastic material of 50 - 150 kg/m³ with a particle size of 1-15 mm (preferably of 5-10 mm) and with a specific surface of 6.0 - 0.2 m²/kg is used.
According to the invention any plastic material wastes or their mixtures can be advantageously and economically utilized. The granules of the required size can be obtained by grinding or milling. For example polyolefines, so polyethylene, or polypropylene, or PVC etc. or their mixtures can be used.
The invention is illustrated by non limiting examples in details as follows:
Preliminary investigation was carried out in order to determine the amount of the grained plastic material to be mixed to the composition for preparing road foundations. A series of 10 kg mixtures of the above composition was prepared with adding different amounts of plastic material ranging from 50 to 200 kg/m³. With adding more than 150 kg/m³ the equal distribution of the plastic material becomes critical, in such cases a lot of plastic material nests are formed in the specimen. The addition of 135 kg/m³ plastic material to the composition consisting of the usual ingredients used for building road foundations and semirigid roadway structures has been found to be optimal.
Specimens of different compositions have been prepared to investigate the compressive strength. The units with indices 1, 2, 3 of the series A, B, C and D, respectively, were prepared without adding plastic material and those with indices 4, 5, 6 contained plastic material.
The meanings of the abbreviations applied are as follows:
Composition of experimental mixtures prepared for the strength test:
The compressive strength of the specimens of the composition above (3 parallel samples for each composi tion) was examined by the Hungarian standard method MSZ 07-3703 on the 21-st day. The results obtained are shown in Table I.
Based on the preliminary laboratory experiments to the following findings can be made:
For the mixture "A" the addition of 173 kg/m³ plastic material does not practically change the value of the compressive strength.
For the mixtures "B" and "D", respectively, some decrease, however, for the mixture "C" an increase of the value of compressive strength can be experienced.
Consequently there is no unambiguous relationship between the plastic material additive added to the mixture in a well distributable amount and the development of compressive strength values, and it can be established that the values of the compressive strength do not decisively deteriorate under the influence of adding plastic material.
Following the preliminary experiments mentioned above we have recommended for bulk production or establishing experimental road stages a mixture containing 135 kg/m³ plastic material additive and having a somewhat higher cement content (140 kg/m³ with the exact composition as follows:
The compressive strength values of this composition are the following (obtained from the average of three samples): 7 days old sample: 3.12 N/mm², 14 days old one:³ .70 N/mm², 21 days old one: 3.36 N/mm².
These compressive strength values significantly exceed the related compressive strength requirements. Based on the above facts the approval of the Ministry of Transport and Communication and that of the builder has been obtained for establishing and constructing the experimental stages.
Main cross-road was built between the villages Komádi and Ujiráz in its planned 250-2+450 section on 25-th, 26-th and 28-th August, 1987. The material was mixed in the mixing plant at Mezpeterd. 40 t refuse granulated and ground plastic material (refuse material of the factory of HMV, Debrecen, Hungary) was utilized.
The compactness in the lower layer as determined by surface probe (the compactness measured according to the Hungarian standard MSZ 14043/7) is equal to 95 per cent, 92 per cent, 93 per cent, 95 per cent, 93 per cent, in the top layer: 92 per cent, 89 per cent, 94 per cent, 95 per cent, 89 per cent,
immediately when completing the construction.
On 6-th October, 1986 according to bending measurement with swinging cantilever:
0.60, 0.55, 0.65, 0.53, 0.40, 0.39 Jm,
and simultaneously according to disc measurement:
E₂ = 327 N/mm².
On l6-th October, 1987 when breaking 21 days old samples:
in average 7.648 N/mm² (7.12 - 8.53) for a density of 2.095 g/cm³ (2.056 - 2.126).
On 21 October, 1987 covering with asphalte.
The results of both bending measurements effected with swinging cantilever and disc measurements performed on the experimental section constructed equally show that the load bearing capacity of the hydraulically bonded road foundation or roadway structure constructed with adding grained plastic material is excellent.
in Debrecen the road with sign l of the settlement Tócosvölgye
0+000-0+100 km approximately 700 m² area and on the service road
0+000-0+155 km approximately on 900 m² area.
On 30-th October, 1987 road with sign l, on l6-th November the service road.
Utilized: 15 tonnes of ground plastic material.
On 5-th December, 1987 covered with asphalte.
The advantages of the invention are as follows:
- As a result of transforming the structure of the hydraulically bonded road foundations the life time of the roadway structure increases, thereby reducing the repair costs and traffic limitations caused by the road repairs,
- as a result of utilizing the plastic material wastes qualified as dangerous ones the environment protection problems caused by storing them can be avoided and the costs of storing can be spared,
- new valuable product is obtained from plastic waste material.
| 标题 | 发布/更新时间 | 阅读量 |
|---|---|---|
| 一种再生型路面结构及其筑路工艺 | 2020-05-12 | 209 |
| 一种防腐蚀混凝土及其用于盐沼泽区筑路或筑桥的应用 | 2020-05-24 | 1039 |
| 一种环保地面硬化剂及其硬化地面的施工方法 | 2020-05-19 | 477 |
| 一种预制渠道伸缩转向节结构 | 2020-05-20 | 699 |
| 电控智能液压振动压路机系统及其控制方法 | 2020-05-15 | 30 |
| 免养生道路无机结合旧料现场再生基层工艺以及道路结构 | 2020-05-18 | 982 |
| 一种节能高效型提钒工艺 | 2020-05-12 | 904 |
| 一种适用于深厚软土路基的处治结构 | 2020-05-24 | 362 |
| 筑路专用复合筛 | 2020-05-11 | 806 |
| 一种带有湿度调节装置的冷铺沥青混合料运输设备 | 2020-05-13 | 424 |
高效检索全球专利专利汇是专利免费检索,专利查询,专利分析-国家发明专利查询检索分析平台，是提供专利分析，专利查询，专利检索等数据服务功能的知识产权数据服务商。
我们的产品包含105个国家的1.26亿组数据，免费查、免费专利分析。
专利汇分析报告产品可以对行业情报数据进行梳理分析，涉及维度包括行业专利基本状况分析、地域分析、技术分析、发明人分析、申请人分析、专利权人分析、失效分析、核心专利分析、法律分析、研发重点分析、企业专利处境分析、技术处境分析、专利寿命分析、企业定位分析、引证分析等超过60个分析角度，系统通过AI智能系统对图表进行解读，只需1分钟，一键生成行业专利分析报告。